2013年6月下第42卷第12期
DOI: 10. 7672/sgjs2013120071
施工技术
CONSTRUCTIONTECHNOLOGY
某泄水闸混凝土裂缝成因分析及防治措施
胡旭方，刘海涛
213135）
（武警水电第二总队第五支队，江苏常州
【摘要】通过对该泄水闸闸坝段混凝土裂缝进行调查分析，裂缝产生的成因主要是基础约束、水泥早期水化热大空气降温等，采取布骑缝钢筋、嵌缝充填微膨胀环氧砂浆等措施进行处理，对裂缝的后期发展进行跟踪观察，提出了有针对性的防治措施。
【关键调】泄水闸；混凝土；裂缝；防治措施
【中图分类号】TU755
【文献标识码］A
[文章编号】1002-8498(2013)12-0071-03
Causes AnalysisandPreventionMeasures on
ConcreteCrackinSomeSluice
Hu Xufang,Liu Haitao
(No. 5 Detachment,No. 2 Hydropower Force of Armed Police, Changzhou, Jiangsu213135,China)
Abstract: By investment and analysis on concrete cracks in some sluice, the authors found that the causes of crack are the restraint of foundation, the big early heat of hydration of cement and the low air temperature ete. The cracks are treated by setting crossing-crack steel bar, filling micro-expansive mortar in the cracks etc. to attain good effect. By tracking the cracks development, some prevention measures are put forward.
Key words:sluice; concrete; cracks; prevention measure
工程概况 1
江西省峡江水利枢纽工程位于江西省吉安市峡江县境内，坝址地处赣江中游，是一座以防洪、发电、航运为主，兼顾灌溉、供水等综合效益的水利枢纽工程。枢纽主要建筑物有混凝土泄水闸、混凝土挡水坝、河床式发电厂房、船闸、左右岸灌溉闸等。工程属I等工程。根据本工程等级，混凝土泄水闸为一级建筑物，泄水闸长355.5m，最大闸高30.5m。
左侧7孔泄水闸闸室段桩号为项横0+ 000.00—0+047.00,坝纵0+175.50—0+304.00 该部位地块岩性多为炭质绢云于枚岩，硅化较明显，呈弱下风化状，劈理密集发育，岩体切割成碎块状，岩体呈碎裂结构，属CIV岩体，岩层层间剪切带发育，性状软弱，宽度一般5~10cm，最宽处达15 30cm，为泥头岩屑，局部夹泥，部分为片理化岩，局部发育有小断层，呈陡倾角，上、下盘接触带为断层泥或廉梭岩，中部为弱下碎块岩。根据设计要求共分7个区，底板分4层，混凝土为Cg25W6F50，混
【作者简介］胡旭方，高级工程师，E-mail;462356211@qq.coe
[收稿日期］2013-02-26 万方数据
71
土砂石骨料采用坝址上游河道天然砂石料进行级配筛分，水泥为南方P.042.5：粉煤灰为F类Ⅱ级粉煤求；外加剂为HAY-2高效减水剂，经试验检测,格
测结果均符合规范要求。 2裂继情况及原因分析 2.1
裂缝情况
泄水闸闸室段1~7号闸室在浇筑第1层（层厚 2.0m）、第2层（层厚0.8~1.3m）后均不同程度出
现多条纵、横向裂缝。 2.2裂缝原因分析
大体积混凝土中产生裂缝的原因有多种，一般认为产生的原因主要是温度和湿度的变化，混凝土的脆性和不均匀性，原材料不合格，模板变形，基础不均勾沉降等。
混凝土表面裂缝多数发生在浇筑初期，而初期的表面温度骤降是引起表面裂缝的主要原因，当目平均气温在2~4d连续下降6~9℃时未满28d龄期的混凝土暴露表面可能发生裂缝，或者龄期3~ 5d拆模的混凝土，使表层混凝土突然暴露在较冷的空气中，也相当于次气温骤降，因为气温骤降在