摘要：阐述了某低压聚乙烯装置生产氯化用聚乙烯用专用树脂粉料QL505P的生产过程、质量改进及放大生产情况。通过优化选择催化剂和催化剂的预络合、降低聚合温度和浆液浓度，
固化生产工艺条件等措施，提高了树脂粉料QL505P的质量，满足了用户要求。关键词：氯化；聚乙烯；专用树脂；质量；改进
中图分类号：TO325.12
文献标识码：B
文章编号：16714962(2017)02003002
Qualityimprovementandproductionenlargementof
specialresinQL505Pusedforpolyethylene Wang Jinghang,Xing Shixuan', Chen Jilao',Zhang Xilai', Wang Song
(1.Plastics Plant of Daqing Petrochemical Company, Daqing 163714, China; 2.Bidding Center of Daqing Petrochemical Company, Daqing 163714, China)
Abstract : This paper expounded the production prxcess, quality improvement and production enlargement of the special resin granule QL 505P used for a HDPE plant to produce chlorination polyethylene, By taking the measures such as optimizing selectior of catalyst and pre= complexing of catalyst, deereasing polymer temperature and slurry condensation and solidifying proxductior
process conditions, the quality of resin granule QL 505P was improved, and the requirement of endusers was satisfied. Keywords: chlorination; polyethylene; special resin; quality; improvement
2012年12月某企业首次工业化生产氯化用聚乙烯用专用树脂粉料，牌号为QL505P。用户提出现有产品颗粒大、氯化难，要求树脂粉料OL505P 的粒径分布范围更加均勾，便于厂家进行氯化为满足用户要求，提高产品竞争力，确保生产的产品粒径分布，在生产工艺上进行研究和改进，优化了生产工艺，降低了聚合温度和浆激浓度，周化生产工艺条件，明显提高树脂粉料QL505P的质量，
自2014年实施以来，产品稳定生产50kt/a以上。 1生产工艺
低压高密度聚乙烯装置生产氯化用聚乙烯树脂粉末QL505P，由原料精制、聚合、脱气、混炼造粒、回收、成品包装等工段组成。聚合过程采用钛系催化剂，按离子聚合机理反应生产。主要原料有聚合级的乙烯、丙烯、氢气等，技术指标见表1。 2质量改进过程
为提高产品质量，符合厂家要求，确保生产的
万方数据
产品粒径分布，在催化剂的选择和使用上进行了
改进，并且在生产工艺控制上进行了优化"]。 2.1催化剂的选择
（1）高密度聚乙烯粉料的形态是催化剂形态的复制和放大.要得到理想的高密度聚乙烯粉料的形态，催化剂的粒径分布要窄并且集中在80目附近.产品的堆积密度还要高。生产过程中改进使用新型催化剂，具有产品堆积密度高，粒径分布均勾细粉含量少的优点，可以进一步改善粉料粒径的分布2
（2）催化剂预络合过程中的AI/Ti比。该措施不仅可以有效合理的控制颗粒的形态向追求的方向靠拢，而目防止聚乙烯颗粒破碎、减少粉末中超细粉含量、显著提高粉末的堆积密度。
（3）改变聚合釜中的己烷、母液混合比，进步脱除超细粉和低聚物，可大幅度改善最终制品的各项物理力学指标。