2017年第1期
炼油与化工
REFINING AND CHEMICAL INDUSTRY
低密度聚乙烯2426H吹膜工艺研究
王世华，葛腾杰，李瑞
（中国石油大庆化工研究中心，黑龙江大庆163714）
摘要：文中对低密度聚乙烯装置生产的LDPE2426H吹膜工艺进行了研究，确定了吹膜生产的最佳条件。结果表明.LDPE2426H的重均分子量为9.4x10°.结晶度为38.5%.具有分子量分布较宽、结晶度较低的特点。在加工温度为170-190、吹账比为3.0时，吹制的薄膜光学性能最好、耐冲击强度高。
关键词：低密度聚乙烯；性能；吹膜工艺；研究
中图分类号：TO325.12
文献标识码：A
文章编号：16714962(2017)01000503
ResearchonfilmblowingprocessforLDPE2426H
Wang Shihua, Ge Tengjie, Li Rui
(PetroChina Daqing Chemical Research Center, Daqing 163714, China)
Abstract: This paper made research to film blowing process for 2426 H produced by the LDPE plant, and determined the best condition for film blowing production. The result showed that the LDPE 2426 H's weightaverage molecular weight is 9.4x10′, its crystallinity is 38.5%, and it has the characteristics of wide molecular weight distribution and low crystallinity. At the temperature of
170190 C and blowup ratio of 3.0, the film blown has the best optieal property and high impact strength. Keywords: LDPE; property; film blowing process; research
某石化公司的低密度聚之烯（LDPE装警采用德国Basell公司的管式法反应器生产技术，设计生产能力200kt/a。该装置主要生产原料为乙烯，以错酸之烯为其聚单体，以内烯或内醛为分子量调节剂，过氧化物为引发剂。采用乙烯单点进料，过氧化物由4点注入脉冲式反应器的生产方式进行生产。低密度聚乙烯的主要特点是具有良好的柔韧性、抗冲击强度高、低透水性以及良好的加工性
能和光学性能，因而广泛应用于薄膜包装行业。 1实验部分
1.1实验原料及主要仪器
实验所用原料为大庆石化公司塑料厂生产的 LDPE 2426 H.
主要仪器：5226型雾度仪.意大利CEAST公司；RH7D型毛细管流变仪，英国ROSAND公司； DSC910型差热扫描仪，美国DUPOUT公司：4667 型控力试验机，美国INSTRON公司：PL-220型影胶色谱仪（GPC），美国WATERS公司；BLU300型吹膜机组，德国Goettfert公司。
万方数据
1.2测试方法
相对分子质量及其分布采用凝胶渗透色谱(GPC)法测试。实验条件：温度160℃，三氯苯为溶剂，流速1mL/min。热力学性能采用差示扫描量热法(DSC)测试。实验条件：样品容器为铜杯
样品量10mg，升温速率10℃/min 1.3吹膜实验
吹膜实验在吹膜机组BLU300（德国）上进行。挤出机螺杆直径为Φ30mm，长径比为20：1，口模直径为60mm，采用风环冷却，薄膜厚度控制
在29~31μm，牵引速率为5m/min。 2结果与讨论
2.1热力学性能分析
对LDPE2426H的热力学性能进行了DSC分析，分析结果见表1。
表1LDPE2426H热力学性能
样品 LDPE 2426 H
熔点%
112.8
结晶温度
99.1
结晶度%
38.5
结晶热(J-g") 89.9
熔融热/( J·g") 116.2