文章编号：1000-033X(2016)09-0053-04
DESIGNANDTESTI段计与试险
基于复掺矿物外掺料的高性能混凝土
配合比设计研究
姚军
（宁波交通工程建设集团有限公司，浙江宁波315000）
摘要：通过“全集算法"对复掺矿粉-粉煤灰矿物掺合料对高性能混凝土进行配合比设计，研究复掺矿粉-粉煤灰的不同比例和不同掺量对高性能混凝土的工作性、力学性能的影响规律。结果表明：当矿粉与粉煤灰的比例为60：40，掺量为胶凝材料总量的35%时，复掺矿粉-粉煤灰矿物掺合料可发挥"超叠加效应”，优化界面过渡区，提高高性能混凝土的密实度，改善高性能混土的耐久性。
关键调：复掺矿物掺合料；高性能混凝土；耐久性；密实度
中图分类号：U414.1
文献标志码：B
ResearchonDurabilityofHighPerformanceConcrete
withMineralAdmixture
YAOJun
(Ningbo Communication Engineering Construction Group Co, , Ltd, , Ningbo 315000, Zhejiang, China)
Abstract; Mix design of high performance concrete combined with mineral admixture was conducted by adopting the overall calculation method, and the impact of the ratio of slag to fly ash and admixture content on the performance and mechanical properties of the high performance concrete was studied. The results show that when the ratio of slag to fly ash is 60 : 40 and admixture accounts for 35% of the binding material, an additive effect occurs between the slag and fly ash, and both the density anddurability of the high performance concrete are improved. Key words: mineral admixture; high performance concrete; durability; density
0引言
高性能混凝土（简称HPC)不仅具有较高的强度，最重要的是具有高工作性、高耐久性，利用高性能混凝土代替传统混凝土以构造在严酷环境使用的混凝土构件，具有明显的经济和社会效益[1-]。
本文基于复掺矿物外掺料的高性能混凝土配合比设计研究，提出适应于对材料有严格技术要求的结构物，如桥梁的复掺矿物外掺料高性能混凝土配合比设计方法。研究结果可为复掺矿物外掺料高性能混凝土的推广应用和发展提供理论基础，具有重要意义。
收稿日期：2016-01-25 万方数据
1
原材料与试验方法 1.1原材料
水泥采用冀东牌水泥P·O42.5。依据《公路桥涵施工技术规范》JTJ041—2000)对粗细集料的物理力学性能和碱活性进行了检测，结果满足规范要求；对细集料进行筛分，筛分结果如表1所示。计算细度模数可知，所用细集料河砂为中砂、粗集料粒径为5~20mm。
所用减水剂为聚酸系高效减水剂。所用水为自来水，水的氯离子含量应小于210mg·L-"，硫酸盐含量按SO-计应小于600mg·L-"，pH值大于5。