聚氯乙烯 Polyvinyl Chloride
月桂酸锌的合成及其红外特征的研究
许家友“，叶柳英，林凯慰，周细滚
（广州大学化学化工学院，广州广东510006）
【关健调]热稳定剂：月桂酸锌；复分解法
Vol.38,No.9 Sep.，2010
[摘要］研究了以月桂酸、氢氧化钠、氯化锌为原料采用复分解法合成月桂酸锌的最佳条件；第1步皂化反应，氢氧化钠过量10%（质量分数），温度80C，反应1.5h；第2步复分解反应，氯化锌过量20%（质量分数），pH值 5~6，快速搅拌，慎温80C。经检测，月桂酸锋中月桂酸质量分数<1%，锌质量分数在13.5%~15.5%，熔点在(128±5）C，均符合标准；月桂酸锋在1580cm"1和1400cm*1之间有2个红外特征峰，R一COO一与Zn主要以络合形式结合。
[中图分类号］TQ314.24
0601600
Study on synthesis of zinc laurate and its infrared characteristics
XUJiayou,YELiuying,LINKaimian,ZHOUXihao
(School of Chemistry and Chemical Engineering,Guangzhou University,Guangzhou 510006,China)
Key words: heat stabilizer; zinc laurate; double dccomposition
Abstract;Zinc laurate was synthesised by using lauric acid, sodium hydroxide and zinc chloride as raw materials, and the optimum reaction conditions are as follows: (1) for saponification reac-tion, the dosages of sodium hydroxide are 10 wt% excessive, reaction temperature is kept constant at 80 C, reaction time is 1.5 h; (2) for double decomposition reaction, the dosages of zinc chloride are 20 wt% excessive, pH value is 56, reaction temperature is kept constant at 80 C, and rapid stirring is needed. The pcrformance test results indicate that: (1) the contents of lauric acid and zinc in zinc laurate are less than 1 wt%, 13.5 wt% 15.5 wt%, respcctively, and the melting point of zinc laurate is (128 ±5) C, which achieve the requirements of product standard. (2) Zinc laurate has two infrared characteristic absorption peaks between 1 580 cm-' and 1 400 cm*', which suggests that R-COO combines with Zn in the form of complex mainly.
Foundation item; Research project of Guangzhou Education Bureau(08C083)
月桂酸锌在塑料、涂料、润清脂、纺织、建筑、造纸、颜额料、日用化学品等领域应用广泛，如月桂酸锌作为PVC热稳定剂应用于塑料工业，作为消光剂等用于涂料工业)。月硅酸锌的合成方法很多，但实际可应用于工业生产的主要是复分解法和直接法[2->]。在国内，月桂酸锌的生产一般采用两步法： ①皂化反应，月桂酸和NaOH中和反应生成月桂酸钠；②复分解反应，月桂酸钠再与ZnClz进行复分解
[收稿日期］2010-06-17
[基金项目］广州市教育局科研项目(08C083)
反应生成月桂酸锌。反应方程式见式(1)、式(2)。
CH,(CH,)COOH+NaOH→
CH,(CH,)COONa+H,O; 2CH,(CH,)COONa+ ZnCl,—
(1)
[CH,(CH,)1COO],Zn + 2NaCI。
(2)
复分解法中，中间产物月桂酸钠胶化能大，在水中溶解度小，溶液黏稠，易包裹ZnClz，致使月桂酸锌的产量和质量达不到要求。笔者用复分解法