耐低温PVC型材配方设计与制造
徐国忠，，张军”
（1.南京华格电汽塑业有限公司，江苏南京210014； 2.南京工业大学材料科学与工程学院，江苏南京210009)
[关键词］PVC型材耐低盈：配方设计
Vol.38, No.11 Nov.,2010
[摘要］重点分析了耐低温PVC型材配方设计的影响因索，并结合实际给出了参考配方和制备工艺。
［文献标志码］B［文章编号】10097937(2010)11-0017-03
[中图分类号］TQ325.3
Formula design of PvC profiles with low temperature resistance and their production
XUGuozhong，ZHANGJun
(1. Nanjing Huage Elcctronics & Automobile Plastic Industry Co. Ltd., Nanjing 210009
2. Collegc of Matcrials Scicnce and Engincering, Nanjing Univcrsity of Technology , Nanjing 210009, China)
Keywords:PVC profilc;lowtcmpcraturc rcsistancc;formula design
Abstract: Factors of influcncing thc formula design of PVC profiles with low tcmpcraturc rc sistancc wcre analyzcd cmphatically. Combining with the practical situations, reference formulas werc givcn as well as thc production process.
Foundation item: Supported by Jiangsu provincial scicntific and technological rcscarch achicvc-mcnts transformation special funds (BA2010017)
PVC树脂由于其结构的特殊性面热稳定性差，很难利用其直接制备塑料制品，因此常常需要在树脂中加人一系列的助剂对其进行改性，以满足加工工艺和实际应用的要求。例如，在PVC制品配方中加入热稳定剂、光稳定剂、内外润滑剂、加工助剂、增韧剂等可提高PVC的物理性能和力学性能(1-3)。 PVC型材由于具有配方成本低、异型结构易于设计与制造、强度和耐候性优异等特点，已经在建筑等领域获得了广泛应用。PVC型材的配方设计受到多种因素的影响，如型材的使用要求、挤出机的工作参数等。因此，合理的配方设计对于保证耐低温PVC 型材的生产和性能至关重要。目前PVC型材主要用于制造塑钢门窗，其具有较高的拉伸强度、弯曲强度和优异的耐紫外光性能，但此类PVC型材耐低温性能差，不能适应特定低温场合对型材的需求，例如
【收稿日期】2010-0921
冷藏柜、箱式冷藏车和冷库等。因此，研究和开发具有耐低温性能的PVC型材对于扩大其应用领域具有一定的现实意义。
笔者针对耐低温PVC型材的实际需求.重点讨论了影响耐低温PVC型材配方设计的因素，包括 PVC树脂、热稳定剂、润滑剂、加工助剂、增韧剂、填料等。另外结合实际介绍了耐低温PVC型材的参考配方与生产工艺。
1耐低温PVC型材原料选择与配方设计 1.1PVC树脂
PVC树脂的性能（如分子质量、分子质量分布等)很大程度上决定了制品的加工性能和最终质量。对于分子质量面言，PVC制品的物理性能和力学性能、耐低温性能和耐热性等均随着分子质量的增加