第39春第10期
2011年10月【加工与应用】
聚氯乙烯 Polyvinyl Chloride
阻燃、耐香烟灼烧PVC地板配方研究
孙宝林”，罗健
（安徽美祥实业有限公司，安徽桐城231400)
[关键词］PVC地板；阻燃；耐香烟灼烧；配方
Vol.39, No.10
Oct.，2011
[摘要］针对客车用软质PVC地板不耐香烟灼烧的缺点，从AI(OHD,/Mg(OHDz、Sb,O,和硼酸锌的用量3个方面对配方体系进行了研究。结果表明：①最佳配方为PVC，100份；DOP，50份；稳定剂，4份；润滑剂，2.5份，*010(HO）份08(HO)V
[中图分类号］TQ325.3
［文献标志码］B
［文章编号］10097937(2011)100022~03
Research on formula for flame retardant property
and cigarette-burning resistant PVC floor
SUNBaolin，LUOJian
(Anhui Meixiang Industry Co., Ltd., Tongchcng 231400, China)
Keywords:PvC floor;flameretardancy; cigarette-burning resistance;formula
Abstract:Aiming at thc shortcomings that soft PVC for bus had no resistance to cigarette burn ing, its formula was studied in dosages of Al(OH)s/Mg(OH)2, Sb,O, and zinc borate. The results show that:@ the optimum formula is PVC 100,DOP50,stabilizers 4,lubricants 2.5,Al(OH)s 80,Mg(OH)40,Sb,O,4,and zinc borate 10 parts; ② Sb,O, has no significant influcnccs on propcrtics of samples without zinc borate.
随着我国交通事业的快速发展，铁路、公路客车不断推陈出新，同时也对客车用地板提出了更高要求。软质PVC地板具有易铺装、美观大方、经久耐用、价廉等优点而得到广泛应用，但由于其中含有易燃的增塑剂，因此降低了软质PVC地板的氧指数还导致其在应用中不耐香烟灼烧而影响美观，给安全也带来了隐患。笔者在普通软质PVC地板配方的基础上，从AI(OH)/Mg(OH)2、Sb,O,、硼酸锌的
用量3个方面对配方体系进行了研究。 1试验部分
1.1主要原材料
PVC(S1000)，中国石油化工股份有限公司齐鲁分公司；邻苯二甲酸二辛酯(DOP)，工业级，金陵石油化工有限责任公司化工一厂；AI(OH)，，工业级，中国铝业山东分公司（经自处理)；Mg(OH)2，市售（经自
[收稿日期］2011-01-24
处理)；SbO，工业级，锡矿山闪星锑业有限责任公
司；硼酸锌、稳定剂、润滑剂，工业级，市售。 1.2试验设备及型号
高速混合机，SHR-10A，张家港震雄塑料机械厂；双辑筒炼塑机，SK-160B，上海橡胶机械厂；平板硫化机，25t，上海第一橡胶机械厂；拉力试验机， DXLL一20000，上海登杰机器设备有限公司；邵氏硬度计，LX-A，江都市明珠试验机械厂；氧指数测定仪，HC-2，江宁县分析仪器厂。
1.3工艺流程及条件 1.3.1工艺流程
配料-→高速捏合→+双辑塑炼-→模压-→+制样→+性能测试。
1.3.2工艺条件
塑炼时严格控制双辊筒炼塑机的辑温在（170士
[作者简介］孙宝林（1960一），男，安徽省桐城市人，1982年7月毕业于安徽省州师范专科学校（现滁州学院)化学专
业，从事高分子材料新产品研发工作。 22