1
引言
模具材料及热处理技术
热处理工艺对大截面锻材
10Ni3MnCuAI性能与组织的影响
岳影超，对明，刘晓，康爱军
113001）
抚顺特殊钢股份有限公司技术中心(辽宁抚顺
【摘要】利用力学性能测试方法及OM、SEM，研究了不同热处理工艺对大截面锻材 10Ni3MnCuAl力学性能与组织的影响。结果表明，固溶前采用正火工艺可提高
化。正火工艺可细化组织和晶粒，但大截面扁钢中心到边部的冷却强度有差异，边角组织细化和品粒细化程度更好。
关键调：正火；10Ni3MnCuAl;组织；力学性能；热处理工艺
中图分类号：TG249;TB497
文献标识码：B
Influence of Heat Treatment Process on Properties and Microstructure
ofLarge-Cross-SectionForgingFlatsof1oNi3MnCuAl
[Abstract] Influence of different heat treatment process on properties and microstructure of largecrosssection forging flats of 10Ni3MnCuAl was studied by mechanical properties tesl method and OM, SEM. The results showed that plasticity and toughness of 1ONi3MnCuAl were improved by normalizing process before solution and aging treatment. The impact value in the center was lower than that at the corner, while the tensile strength did not change significantly. Microstructure and grain size were refined by normalizing process. However, the quenching cooling strength from center to corner of largecrosssection flats was different, the microstructure and grain size refinement at the corner was better.
Key words: normalizing; 10Ni3MnCuAl; structure; mechanical properties ; heat treatment process
艺，研究了10Ni3MnCuAI钢截面不同位置的组织及
随着塑料制品的快速发展，大型塑料模具钢的需
求也越来越大。10Ni3MnCuA1为超镜面塑料模具钢，具有良好的镜面加工、焊接性能和花纹图案雕刻性能等。模具使用过程中要求钢材具有良好的强度、塑韧性和耐磨性等力学性能，尤其大截面锻材的心部质量急需提高。适当的热处理工艺可改善大截面 10Ni3MnCuA1钢不同位置的各项性能"-3)。
抚顺特钢生产的锻材多年来成为国内的领先品牌，但是与国际先进水平相比，在冲击韧性等方面存在较大差距4-}，尤其大截面锻材中心到边角差异较大，不均勾程度较明显。本文利用不同的热处理工
《模其制造》2018年第8期
万方数据
各项性能，为生产及使用提供了有效的依据。
2
试验材料、工艺及方法
试验材料
2.1
试验材料的化学成分如表1所示，试验材料的冶炼工艺为：电炉冶炼，LF精炼炉和VD脱气，电渣炉重熔钢锭，3.500t压机锻制成材，成材后的截面尺寸为 550x1,100mm。
试验工艺
2.2
两块试验钢采用的热处理工艺如表2所示。
·83.