：模具材料及热处理技术：
模具材料及热处理技术
热处理工艺对塑料模具钢1ONi3MnCuA
组织、晶粒度和性能的影响
冯淑玲，刘明
抚顺特殊钢股份有限公司（辽宁抚顺113001）
【摘要】利用金相和冲击试验方法测定了10Ni3MnCuAI正、回火和泽、回火处理后的组织、晶粒度和冲击韧性。结果表明，试验钢通过正火可显著改善组织均匀性和细化晶粒，晶粒度由淬、回火状态的2级提高到7级，950℃为试验钢的最佳正火温度；试验钢经过950℃正火和520C回火处理后组织为回火贝氏体，回火后硬度为41.3HRC，冲击值达到13.3J，相对
880℃漳火和520℃回火冲击值有显著提高：关键词：正火；10Ni3MnCuAl；组织；晶粒度
中图分类号：TG142.45：TG659
文献标识码：B
Effect ofHeatTreatment ontheMicrostructure,Grain Size
and Properties of Plastic Die Steel 10Ni3MnCuAl
[Abstract] In this paper, microstructure, grain size and the impact toughness of normalizing. tempering and quenching, tempering of 10Ni3MnCuAl have been test by using the metallographic and impact. The result show that, microstructure and grain size of the test steel have been uniformity and refinement by normalizing. grain size increased from 2 grade of quenching and tempering to 7 grade, 950°C is best normalizing temperature of tested steel; Microstructure of the test steel was Tempered Bainite through 950°C normalizing and 520°C tempering, tempering hardness was 41.3HRC,the impact value was 13.3J, significantly improving compare to 880°C quenching and 520°Ctempering.
Key words: normalizing; 10Ni3MnCuAl; microstructure; grain size
1引言
随着塑料制品的快速发展，对高档镜面塑料模具钢的质量要求越来越高。其中具有代表性的钢种 10Ni3MnCuAl.是一种析出硬化型的低碳合金钢.具有良好的率透性、耐蚀性、抛光性、图案雕刻性能等。不过，在不同的使用条件下，不仅要求钢材具有良好的工艺性能，而且其机械性能、耐热和耐蚀性等更应具备。目前，对于10Ni3MnCuAI钢热处理工艺的研究较多-3] 而且提出了不同的观点。10Ni3MnCuAI钢淬、回火处理后的晶粒尺寸粗大，细化晶粒尺寸和改善组织均匀性可以明显提升综合力学性能，正确的热处理工艺是影响晶粒度和组织的关键。本文研究了10Ni3MnCuAI
· 82· 万方数据
钢在不同热处理制度下的组织、晶粒度和冲击值变化，为提高钢材质量和综合力学性能提供参考。
2试验材料及方法 2.1试验材料
试验钢的冶炼工艺为：电炉冶炼，LF精炼炉和VD 脱气，经电渣炉重熔成930mm钢锭，采用3.500t快锻机锻制成材.截面尺寸为350x660mm。其化学成分如表1所示。
表
试验钢的合金成分（质量分数，%）
Mn
0.13
0.22
S
p
Ni
0.0050.020
13.05
Cu F0.90
Al
Mo
Fe
1.080.30Bal.
《模具制造》2017年第7期