1引言
·挤压模技术·
浅析挤压温度对磁轭温挤压模具的影响
陈琳
长江工程职业技术学院机械工程系（湖北武汉430212）
【摘要】通过有限元分析软件DEFORM-3D对4Cr5MoSiV1材质的磁轭温挤压模具进行了分析，找出了挤压温度对磁轭温挤压模具温度、模具挤压力、凹模载荷、模具应力的影响分析。试验证明：随着挤压温度升高，挤压力下降，模具应力小，特别是挤压终了时凹模载荷小，模具发生塑性变形倾向小；然而，挤压温度越高，工件挤压终了时模具表面温度越高，
会使模具出现冷热疲劳造成模具早期失效。关键词：模具；温挤压；挤压温度；有限元；失效
中图分类号：TG372
文献标识码：B
Analysis of the Influence of Extruding Temperature on the Magnetic Yoke Temperature Extruding
[Abstract]The article does the analysis of 4Cr5MoSiV1 material of magnetic yoke temperature extruding die through the finite element analysis software DEFORM3D, in order to find out the influence of the extruding temperature on the die temperature, the die extruding force, the die load and the die stress of the magnetic yoke temperature extruding. The test shows that followed the extruding temperature decreased, extruding force is reduced, and the die stress is small. Especially, the die load is small at the end of extruding, and the plastic deformation tendency of the die is small; However. the higher the extruding temperature, the higher the die surface temperature at the end of the extruding, the mold will appear hot and cold fatigue, resulting in early failure of the mold.
Key words: die; warm extruding; extruding temperature; finite element; failure
为研究这些工艺因素对温挤压成形过程的影响，
近年来，随着模具工业的发展，模具作为机械加工工艺装备的常见形式之一，其寿命高低、性能的好坏直接关系到制件质量和社会效益。分析和研究影响模具失效的原因，采取相应的有效措施能提高模具使用寿命，并能较好地产生经济效益。变形温度、变形程度、变形力、变形速度、模具材料、模具结构、摩擦等是温挤压变形过程的基本因素，这些因素直接影响着模具的早期失效和寿命。本文通过有限元分析软件DEFORM-3D对4Cr5MoSiV1材质的磁轭温挤压模具进行分析，找出挤压温度对磁轭温挤压模具影响。
2模拟方案的制定
62: 芳方数据
利用DEFORM软件对磁轭温挤压成形过程进行三维刚粘塑性有限元数值模拟。现对圆柱毛坏在不同的挤压温度条件下，温挤压成形磁轭的过程进行有限元数值模拟研究，找出不同工艺参数对磁轭温挤压成形的影响状况和影响模具早期失效的因素，从而为进一步分析模具早期失效提供依据。挤压模型为磁轭模型，模具材料为4Cr5MoSiV1，挤压材料（工件）为 40Cr，初始毛坏尺寸：Φ40.5×32.16mm，其几何形状如图1所示。毛坏与模具间的摩擦系数：0.25；环境温度：室温20℃；挤压温度：500℃、550℃、600℃、650℃、 700℃、750℃、800℃。
《模具制造》2017年第10期