干熄炉斜道区砌筑经验和探讨
徐昶辉刘杰杜镇钢
（宝钢股份炼铁厂炼焦分厂，上海20094
Sep.2013 Vol. 44 No.5
摘要：在分析国内干熄炉斜道损坏情况的基础上，结合宝钢四期干熄炉砌筑特点，提出了膨胀缝分3段技术、氮化硅结合碳化硅砖技术、斜道“牛腿”中心精确定位技术、斜道区过顶砖拱形过顶技术以及严格控制标高和内径的方
法来确保斜道砖砌筑质量，延长干熄炉的使用寿命。关键词：干熄炉；斜道砖：砌筑技术
中图分类号：TQ522.16
文献标识码：B
文章编号：10013709（2013）05003003
ResearchofbricklayingforCDQconnectingduct
Xu Changhui Liu Jie Du Zhengang
( Coking Plant of Baosteel Co , Ltd. ,Shanghai 200941 , China)
Abstarct: According to the damage of CDQ connecting duct in China and the features of CDQ brick-laying in Phase IV of coking project for Baosteel , new technologies have been put forward, such as three-segment expansion joint , silicon nitride and silicon carbide bonded brick , precise-position at center of connecting duct as well as accurate elevation and inner diameter so that the CDQ connecting duct bricks can be laid in good quality and the service life of the CDQ chamher can be extended -Key wods : Dry quenching chamber ; Connecting duct brick ; Bricklaying technology
干熄焦技术对减少环境污染、节省水资源能源
再利用和提高焦炭质量具有重要作用和意义。近儿年来，干熄焦工程虽然建设很多，但能常年正常使用的较少。干熄焦斜道区（俗称“牛腿”）质量达不到设计和使用年限损毁严重，导致干熄炉停产检修是一大制药因素。宝钢四期炼焦沿装一、二、三期炼焦成功经验，熄焦仍采用全干熄技术，在斜道区砌筑方面，充分总结了以往经验及不足，采用一系列新方法，其千熄炉处理能力较一、二、三期有所提高
1干熄炉斜道砖损坏原因分析 11化学腐蚀
内衬砖在高温CO、H，等还原性气体作用下易发生还原腐蚀"。此外在1000℃环境中，也会发生氧化反应，氧在裂纹尖端与SiC发生如下反应形成含有杂质的硅酸盐晶界薄层，即氧化膜层。
2SiC +302→2SiO2 +2CO ↑ 收稿日期：2012-12-29
作者简介：徐租辉（1984→），男，助理工程师
氧化过程包括氧离子在裂纹尖端的传递、SiC一 SiO2反应、CO从反应区域析出3个阶段。氧化膜的形成是控制裂纹扩展的主要因素。SiC材料的裂纹生长受氧化膜的塑性效应以及随后的热激活键断裂控制。
1.2裂纹成核及扩展
斜烟道部位目前大部分都采用莫来石结合碳化硅砖，由于材料上存在设计和加工的缺陷，以及材料内部或表面非均质的裂纹成核部位都会产生应力，局部应力超过材料的抗折强度2，产生显微范围内局部塑性变形，随着循环应力的继续，形成尖锐的裂
隙，在一定部位上裂隙穿入基体发展成裂纹。 1.3热应力损伤
斜道区由于反复升降温造成耐材冷热收缩加剧，急冷急热条件下产生热应力了，在热冲击循环作用下，材料先出现开裂、剥落，然后碎裂或变质，最终整体损坏。