LY12铝合金A-TIG焊活性剂研制
孔兆财"，夏桂海”，林三宝”，季相儒”
（1.首都航天机械公司北京100071;2.哈尔滨工业大学先进焊接与连接国家重点实验室黑龙江哈尔滨150001）摘要：针对LY12铝合金，利用正交试验法研制A-TIC焊接的活性剂，选用NaCI，NaF，CaF，混合物作为活性剂。实验发现当三者质量之比为1：1：2时焊缝深宽比最大。焊接过程中电弧在未涂的铝板上主要为扇形，当电弧过渡到涂敷活性剂一侧时，由扇形变为钟罩形，电弧收缩，热量集中，熔深增大，此外由于焊接过程中活性剂存在，电弧左右快速摆动，增加了熔宽。
关键调：铝合金；A-TIC焊；活性剂中图分类号：TG444+.72
DevelopmentofactivefluxesforLY12aluminumalloyA-TIGwelding
Kong Zhaocai',Xia Guihai’,Lin Sanbao', Ji Xiangru
(1.The Capital Aerospace Machinery Company,Beijing100071,China;
2. State Key Laboratory of Advanced Welding and Joining,Harbin Institute of Technology,Harbin 150001,China) Abstract: In this paper, active flux for LY12 aluminum alloys was developed. The active fluxes are the mix-tures of NaCl,NaF and CaF2. When they were mixed in proportion of 1:1 :2, the depth-lo-width ratio of the welded joint is the highest. The arc shape turms from fan-shaped to bell shaped when it burms on the fluxes coa ted place. The arc constrict and the welding energy are concentrated, so that the penetration depth increases.
The arc works on the active flux and swings to increase the weld width. Key words: aluminium alloy; A-TIG welding; active flux
0前言
活性化非熔化极气体保护焊（Activating-FluxTIG）从理论提出到如今，国内外学者对这项技术进行了研究[1-2)。活性化非熔化极气体保护焊（A-TIG)就是通过在试件表面涂敷活性剂材料的方式，改善电弧形态、熔池流动等来增加焊缝熔深，进面提高焊接效率的焊接方法。
相比于常规TIC焊，A-TIG焊技术有以下优点[3-5]：①提高焊接生产效率；②减少焊接变形：③熔深基本不受板材中微量元素变化的影响。常规TIG焊
基金项目：国家科技支撑计划项目（2015BAF01B00）
6
2017年第2期万方数据
不能满足实现较大熔深的焊接要求，凭借以上优点A， TIG焊越来越受到焊接科研者与生产者的关注。A-TIG 可显著的增加焊缝熔深(6-7)，相比于传统TIG焊而言， A-TIG焊可节省--半的焊接时间，并达到常规TIG焊两倍的熔深，很大程度上提高了生产效率。
受轻量化理念的推动，目前在工业生产中，铝合金凭借优良的性能使其逐渐得到广泛应用。如今A-TIG 焊活性剂主要用在不锈钢和钛合金焊接领域中。目前针对铝合金A-TIG焊的活性剂研究及相应工艺的开发较少，市场待研发出一种适用于铝合金的A-TIG焊活性剂并开发出相应的焊接工艺。针对LY12铝合金，选