承钢连铸中间包水口粘结原因及改进
营永煜
（河钢集团承钢公司板带事业部，河北承德067002）
Total No.263 2017,Numberl1
摘要：介绍了承钢SPHC铝镇静钢的生产工艺，分析了低碳铝镇静钢浇铸过程中间包水口粘结现象的原因，并分别针对温度和Al,O，引起的低温絮流制定了相应的改进措施。实施后，连铸水口絮流现象得到
有效解决，大于30μm的Al,O；夹杂基本去除，连铸机生产稳定、正常。关键词：中间包水口；粘结：温度；AlO
中图分类号：TF775
文献标识码：B
doi:10. 13630/j. cnki. 13 1172.2017. 1115
文章编号：10065008(2017)11005804
REASONANDIMPROVEMENTOF
NOZZLESTICKINGINCHENGSTEELTUNDISH
Gong Yongyu
( Strip Department of HBIS Group Chengsteel Company, Chengde, Hebei, 067002)
Abstract : This paper introduced the production process of SPHC aluminum killed steel, analyzed the reason of tundish nozzle sticking of low carbon aluminum killed steel, and the corresponding improvement measures for low temperature flocculating flow caused by temperature or Al,O, were also made. After the implementation, the flocculating flow in nozzle has been effectively solved, the Al,O, inclusions larger than
30 μm are basically removed, and the production of the caster is stable and normal. Key Words: tundish nozzle; sticking; temperature; aluminum oxide
0
引言
承钢公司在连铸生产过程中，多次发生过中间包水口堵塞的现象，使拉速降低甚至铸流中断。中间包水口内的粘附物还可引起浸入式水口偏流，引起裹渣，产生裂纹等，给正常生产带来一定的影响]。据统计因水口堵塞造成的中间包非计划停用数量约占3.7%。中间包水口堵塞的问间题，国内外的专家们也已进行了较多的研究，借鉴专家们的经验，笔者对本单位的中间包水口运行情况进行了长期跟踪分析。
在钢的连铸过程中，浸人式水口的作用是控制中间包向结晶器铸人的钢水量和结晶器内的钢水流动，它对稳定操作和确保钢水质量起到非常重要的
收稿日期；2017-0804
作者简介：宫永煜（1979-），男，助理工程师，2014年毕业于河北联合大学冶金工程专业，现在河钢集团承钢公司板带事业部工作，E-mail :596503145@ q- com
58
万方数据
作用。当Al2O，粘附在浸入式水口内壁时，结晶器内会发生水口铸流的偏流现象和钢水面的波动，不仅会恶化连铸坏的质量，而且严重影响多炉连铸的实现[2]。
工艺概况 1
SPHC铝镇静钢是承钢公司的主要品种之
该钢种采用BOF顶底复吹-LF精炼炉-连铸机生产工艺路线。该钢种在浇铸过程经常出现中间包水口粘结现象，从而影响正常生产，造成非计划停浇。
2
原因分析
中间包水口堵塞主要有2种现象：一种现象是
各种原因导致的钢水低温絮流，停浇水口中的粘结物外圈深灰色而内圈是少量白色物体，取样分析，成