配加新西兰海砂生产实践
徐桂芬
（河钢集团承钢公司炼铁部，河北承德067002）
Total No. 245 2016,Number5
摘要：依据实验室烧结杯试验结果，确定了新西兰海砂在钒钛矿烧结生产中的合适配比为10%~15%。在烧结机配加后，通过改进松料器、利用蒸汽预热、控制适宜的烧结矿碱度强化混合料成球增强料层透
气性等措施，保证了烧结矿产品质量，转鼓强度满足了高炉生产需要。关键调：新西兰海砂；烧结杯试验；生产实践
中图分类号：TF046.4
文献标识码：B
doi:10.13630/j. cnki. 13 1172.2016.0511
文章编号：10065008(2016)05003804
PRACTICETOADDNEWZEALANDIRONSAND
XuGuifen
( Iron Making Department, Hesteel Group Chengsteel Company, Chengde, Hebei, 067002)
Abstract: Based on sintering pot test in laboratory, the suitable proportion of New Zealand iron sand in vana-dium titanium ore sintering production is determined as 10 to 15 percent. With measures; improving charge releaser，utilizing vapor to pre heating, controlling suitable sinter basicity,strengthening mixing materialsballing, improving air permeability of materials layer, the quality of sinter is guaranteed, its drum strength can meet demand of blast furnace production.
Key Words: New Zealand iron sand; sintering pot test; production practice
引言
当前钢市菱靡，如何降低成本成为各钢企生产
经营工作的主题。对于以锐钛磁铁精矿为主要烧结原料的钢铁企业，导找到一种性价比高的含钒钛的铁精矿代替当地钒钛磁铁精矿极为必要。在低价外矿中，新西盖海砂含有钒钛成分，可以提供钒钛矿生产所需的钒资源。因此，承钢公司购进10000t新西兰海砂，拟在烧结机尝试配加。
新西兰海砂产于新西兰近海滩，是由海水冲刷作用形成的天然含铁矿物，储量非常丰富，价格低廉，货源稳定。其铁品位低于58%，V,O，、TiO， AI,O，含量都比较高，属难烧矿物，而其粒度又较（小于0.074mm的仅占10%），比表面积小，湿容量小，对水敏感，成球性差，对于以钒钛磁铁矿为主要含铁原料的烧结生产很不利。本次工业试验的目
收稿日期：2016-0224
作者简介：徐桂芬（1972－），女，工程师，1992年毕业于河北省冶金工业学校钢铁冶金专业，现在河钢集团承钢公司炼铁部从事烧结技
术工作，Emsil:xx_sj_xugfe 163.com 38
万方数据
的是摸索新西兰海砂在钒钛矿生产中合适的配比，并跟踪其对烧结生产的影响。
生产实践过程
因新西兰海砂对水敏感，成球性差，从而造成烧结料层透气性变差，导致烧结矿产量和质量下滑，所以工业生产中应考虑确定合适的配加比例并采取有效的措施改善成球效果，以减小其带来的负面影响。确定合适的配加比例依靠实验室烧结杯试验来完成，而采取的改善成球效果的措施应根据现场实际情况确定。
实验室烧结杯试验 1.1
1.1.1试验所用原料及成分
试验所用原料及成分见表1。 1.1.2
试验方案及结果
试验方案及结果分别见表2、表3。