刘建培
（河钢集团石钢公司技术中心，河北石家庄050031）
Total No. 261 2017,Number9
摘要：利用温度跟踪记录仪，采用黑重子测温技术，对GCr15轴承钢大型连铸坏加热过程进行了多点连续温度测试，分析了钢坏的实际加热温度场随时间的变化过程及温度均匀性。为优化加热制度，降低产
品缺陷，提高生产过程控制能力和实物质量水平提供了借鉴。关键调：轴承钢；黑厘子：温度测试
中图分类号：TF762.4
文献标识码：A
doi;10. 13630/j. cnki. 13 1172. 2017. 0907
文章编号：10065008(2017)09002304
CONTINUOUSMEASUREMENT OFREHEATINGTEMPERATUREOF
BEARINGSTEELCCBLOOMWITHLARGESECTION
Liu Jianpei
( Technical Center, HBIS Shisteel Company, Shijiazhuang, Hebei, 050031)
oeeaae reheating process of large continuous casting billet of GCr15 bearing steel was tested for its multi - point continuous temperature, and the change of actual reheating temperature field of the bloom along with the reheating time as well as the uniformity of the temperature are analyzed. It provides a reference for optimizing heating system, reducing product defects, improving production process control capability and material quality level of produc.
Key Words; bearing steel; black box; temperature measurement
0
引言
在特殊钢棒材的生产过程中，有很多产品缺陷
涉及加热过程的控制。如轴承钢的碳化物液析、带状问题，弹黄钢的脱碳问题，齿轮钢的带状间题，钢坏热应力裂纹间题，氧化铁皮除不净问题等等，这些问题都与钢坏的实际加热温度及温度变化过程有关。采用合理的加热工艺是加热炉实现优质、高产、低能耗的关键。要了解掌握加热炉内实际执行的热工制度或寻找最佳的热工制度，就有必要进行锅坏温度的在线测量。通过对钢坏不同部位升温及炉气温度的实测，掌握加热炉炉气实际温度分布及钢坏温度场的动态变化。结合加热钢种的特性、生产及质量状况，发现炉子操作、结构、热工制度等方面的
收稿日期：2017=05-26
作者简介；对建培（1971－），男，工程硕士，高级工程师，2015年毕业于北京科技大学材料专业，现在河钢集团石钢公司技术中心负责轧
钢工艺技术研发工作，E-mail:liu_jianpei@163.com 万方数据
间题，最终通过优化加热制度和操作，以最低的成本生产满足质量要求的产品。
本测试就是通过实际跟踪测试步进梁加热炉的加热过程，对典型坏型和钢种的钢坏加热温度进行在线多点连续跟踪测试，获得钢坏多点连续的温度数据。通过分析获得钢坏的实际加热温度场随时间的变化规律，为优化加热制度，降低轴承钢的碳化物带状级别，提高轴承钢生产的过程控制能力以及实物质量水平提供指导。
测试基本情况加热炉基本参数
1.1
型式：上下加热步进梁加热炉。进出料方式：单排装料，侧进侧出。
加热炉主要尺寸：有效长度38000mm，内宽 6600mm。
加热能力：冷装额定产量130h，热装最大产量150/h。
23