宣钢4#高炉长寿技术应用实践
张洪海
（河钢集团宣钢公司炼铁厂，河北宣化075100）
Total No. 250 2016,Number10
摘要：高炉长寿是一项系统工程。宣钢4高炉采取合理设计、严格施工、高炉精细操作、管控有害元素炉体维护等技术措施，一代高炉寿命已经达到了10年8个月，达到了预期的长寿目标，目前正在步人大型高炉长寿的先进行列。
关键调：高炉；长寿技术；应用
中图分类号：TF546
文献标识码：B
doi: 10. 13630/j. cnki. 13 1172. 2016. 1012
文章编号：10065008(2016)10004803
APPLICATIONPRACTICEOFLONGWORKLIFE TECHNIQUEINBLASTFURNACE4OFXUANSTEEL
Zhang Honghai
(Ironworks, Hesteel Group Xuansteel Company, Xuanhua, Hebei, 075100)
Abstract: To get a long work life for a blast furnace is a system project.A series of technical measures is adopted for blast furnace 4 of Xuan Steel: reasonable design, strict construction, fine operation, managing and controlling harmful elements, furmace body maintenance, its one generation life has reacted to one year plus eight months, the expected target. At present it is stepping into the adva iced line of long life large scale blast furnace.
Key words: blast furnace; long work life; application
引言
随着钢铁业的不断发展，高炉长寿不仅能节约
大修费用，改善高炉技术经济指标，增加生铁产量，而且能充分发挥铁前工序的设备能力，提高企业的经济效益。因此，炼铁工作者越来越重视高炉长寿效益和高炉长寿的研究，实现钢铁联合企业的高效化、连续化得到正常有序进行。国外高炉在长寿方面处于先进水平，高炉寿命大多数在10~15年之间，部分高炉寿命超过了15年。我国大多数高炉的寿命都在6~8年之间，与国外高炉有很大的差距。
宜钢4#高炉有效容积1800m，于2005年10 月24日建成投产，截至2016年7月份已经生产了 10年9个月，生铁产量总计1609.18万t,单位炉容生铁产量8940m。目前还在生产，炉红炭砖温
度200~250℃，高炉寿命有望进一步延长。收稿日期：201608-19
作者简介：张洪每（1971-），男，工程师，2010年毕业于河北理工大学钢铁冶金专业，现在河钢集团宣钢公司炼铁厂从事高炉炼铁工作，
电话：13933992209 48
万方数据
长寿化设计及施工
宣钢4#高炉以“先进、长寿、经济、环保”为设计原则，主要特点是大炉缸、加深死铁层、适当矮胖、减小炉身和炉腹角。炉缸高度4300mm，炉缸容积占高炉有效容积的18.75%，保证风口前有足够的风口回旋区，有利于煤粉的充分燃烧和改善高炉下部中心焦的透气（液）性，有利于改善气体动力学条件。死铁层深度2143mm，死铁层深度占炉缸直径的21.43%，减轻铁水环流造成的“象脚"状异常侵蚀，提高炉缸、炉底寿命。为适应宣锅原燃料条件，炉型适度矮胖，高径比2.41，适当减小炉腹角，有利于炉内煤气流均匀分布，延缓对炉腹、炉腰冷却壁的冲剧、损坏，延长炉体寿命。
4#高炉采用陶瓷杯炭砖水冷炉底、炉缸结构，炉底下部砌筑一层石墨炭砖、三层半石墨炭砖，炉底上部砌筑微孔炭砖，炉缸外侧环砌炭砖，炉缸内为陶瓷杯结构。铁口区域和铁口以下的杯壁厚度逐渐增厚，并与陶瓷垫形成平滑过渡的“锅底”型热面，风口区域采用与陶瓷杯壁相同材质的单元式大块风口