宣钢2#高炉护炉操作技术
王聪渊
（河钢集团宜钢公司炼铁厂，河北宣化075100）
Total No. 259 2017,Number7
摘要：宣钢2#高炉铁口区域炭砖温度升高，已经威到安全生产，必须采取措施加以维护。根据3#铁口区域炉缸炭砖温度升高情况，采取了提高冷却水量、堵风口、提高钛负荷、优化上、下部制度，强化过程参数控制、加强外围协调组织等一系列的护炉技术措施，护炉效果十分显著，同时又实现了炉况长期稳定顺行和技术经济指标的提升。
关键词：高炉；护炉；技术经济指标
中图分类号：TF543
文献标识码：B
doi : 10. 13630/j. cnki. 13 1172. 2017. 0716
文章编号：10065008（2017)07006304
PERATIONTECHNOLOGYOF2#BLAST FURNACEPROTECTIONOFXUANSTEEL
WangCongyuan
(Ironmaking Plant, HBIS Group Xuansteel company, Xuanhua, Hebei, 075100)
Abstract : Carbon brick temperature of iron notch of 2# BF in Xuansteel was rised, which had been a threat to the safety production, so measures must be taken. According to the rising temperature of hearth carbon brick in 3# iron notch, a series of furnace protection measures were taken, such as increasing cooling water volume, blocking tuyere, improving titanium loading, optimizing upper and lower system, strengthening process parameter control,strengthening peripheral coordination organization.The effect of furnace protection is very remarkable, meanwhile the long term, stable and smooth operation is realized and the technical and economic indexes are improved.
Key Words : blast furnace; furnace protection; technology and economic indicator
引言
河钢集团宣钢公司炼铁厂高炉作业二区2#高
炉于2010年9月18目建成投产。炉缸、炉底采用石墨炭块-陶瓷砌体复合炉衬，结合水冷薄炉底炭砖结构。炉底从下至上分别础筑国产超导石墨砖、国产半石墨砖、国产微孔炭砖和超微孔炭砖，共4层（每层高约400mm），炉底最上部砌筑陶瓷杯砖（高约800mm），炉缸外侧环砌进口德国小块炭砖（高约4600mm），炉缸最上部环砌3层国产微孔炭砖（每层高约400mm），炉缸内侧陶瓷杯采用全杯结构（高约5000mm）。炉腹、炉腰及炉身下部采用4 段铜冷却壁。炉身中上部采用镶砖冷却壁，炉底、炉
收稿日期；2017-04-02
作者简介：王聪渊（1975－），男，工程师，2012年毕业于河北联合大学冶金工程专业，现在河钢集团宣钢公司炼铁厂从事炼铁工作，E mail : wangcongyuan@ xuangang. com. cn
万方数据
缸采用俄罗斯的FK侵蚀监测系统。2016年12月8 日3#铁口区域T04092、T04083炭砖温度升高至597 ℃、642℃，已威胁到安全生产，必须引起高度重视，采取必要措施进行护炉，确保安全生产。截止2017 年1月份2#高炉已生产6年多，属于炉役中后期，进人1月份后铁口区域炉缸侧壁炭砖温度突然上升现象。高炉采取了提高冷却水量、堵风口、提高钛负荷等一系列的护炉技术措施，通过优化上、下部制度，强化过程参数控制、加强外围协调组织等措施、护炉效果十分显著，同时又实现了炉况长期稳定顺行和技术经济指标的提升"。
2017年第一季度2#高炉护炉期间的技术经济指标见表1。
63