钒钛矿高炉应对
原料含钒变化的生产实践
邵患斌
（河钢集团承钢公司炼铁事业部，河北承德067002）
Total No.261 2017,Number9
摘要：介绍了钒钛矿中型高炉在含钒原料比例大幅增加情况下采取的应对措施。通过加强对矿情筛分的管理，控制落地钒烧结矿人炉时间，逐步置换；下调焦炭负荷0.1以上，增加焦炭层厚度；对矿石和焦炭的环数和角度进行调节，适当加重边缘负荷；降低【Si】+【Ti]至0.2%~0.3%之间.物理热在1420~
1440℃之间，严格控制铁间隔30min、见查时间30min，保证了高炉稳定顺行。关键调：高炉；高钒烧结矿；透气性：煤气流
中图分类号：TF542.2
文献标识码：B
doi:10. 13630/j. cnki. 13 1172. 2017. 0911
文章编号：10065008(2017)09003904
PRODUCTIONPRACTICETOADAPTTOTHE
VANADIUMCONTENTCHANGEINRAWMATERIALS
FORTHEBLASTFURNACETOUSEV-TI-BEARINGORE
DiHuibin
(Iron Making Business, HBIS Group Chengsteel Company, Chengde, Hebei, 067002)
Abstract: This paper introduces the measures adopted in V - Ti - magnetite BF in the case of substantial increase in the proportion of vanadium containing raw materials, The stable operation of the blast furnace is guaranteed through strengthening the management of groove screening, controlling the charging time of vanadium bearing sinter, gradually replacing: reducing the coke load by more than O. 1, increasing the thickness of coke layer; adjusting the ring number and angle of ore and coke to appropriately increase the edge load; reducing [Si] + [ Ti] to 0. 2% ~ 0. 3% , the physical heat at 1 420 ~ 1 440 C, strictly controlling the interval between two tapping time less than 30 min, the time from taphole opening to the outflow of slag lessthan30min.
Key Words: blast furnace; sinter with high vanadium content; permeability : gas flow
引言
钒钛矿中型高炉炉体采用全冷却壁结构，共14
段冷却壁，其中3段为铜冷却壁，在炉身处8段和11 段分别设置4个静压监测点，通过铜冷水温差的变化情况能够及时掌握炉况变化情况，指导高炉操作。钒钛矿中型高炉正常生产时生产含钒铁水，铁水含钒量0.2%~0.3%。2015年受环保和市场因素影响，降低铁水含钒至0.2%以下，炉况稳定，2015年
收稿日期：2017-05-22
作者介：邸惠斌（1983－），男，助理工程师，2006年毕业于山西工程职业技术学院冶金工程专业，现在河钢集团承钢公司炼铁事业部
I作,Email: xx_It_dihb@ edvt. com.cn 万方数据
7月23日受烧结机检修影响，原低钒烧结矿不能供应，被迫配吃落地高钒烧结矿。烧结矿钒含量的变化势必对高炉生成造成影响，本文介绍了应对烧结矿钒含量变化高炉秤采取的措施。
高钒烧结矿入炉的控制
钒钛矿中型高炉一直采用高碱度烧结矿+酸性球团矿+少量生矿的炉料结构，烧结矿配比达70% 左右。由于落地烧结矿堆放时间较长，粉化严重，并且需要通过汽车运输，进一步使烧结矿的粒度下降，使人炉前的烧结矿含粉量大幅增加。烧结矿的调整及筛分情况如表1、表2所示。
39