不同造渣剂在转炉半钢炼钢中的应用
何凯
（河钢集团承钢公司，河北承德067002）
Total Ne.253 2017,Numberl
摘要：针对半钢炼钢渣系组元单一，化渣困难，使用萤石造渣时对炉村侵蚀产重等问题，通过研究机烧尾矿、铁矾土、钢包渣等不同造渣剂在转炉半钢炼钢中的应用，成功替代了传统的董石化渣工艺，得到了经
济合理的半钢炼钢造渣工艺，提高了半钢炼铜化渣效果。关键词：半钢炼钢；钢包渣：铁矾土：机烧返矿：造流
中图分类号：TF713.3
文献标识码：B
doi;10. 13630/j. cnki. 13 1172. 2017.0108
文章编号：10065008(2017)01003304
APPLICATIONOFDIFFERENTSLAGMAKING AGENT IN STEELMAKING WITH SEMI-STEEL
HeKai
( Hesteel Group Chengsteel Company, Chengde, Hebei, 067002)
Abstract; To solve the problems in steelmaking with semi steel; only single component in slag system, slag melting difficult, serious corrosion on furnace lining when using fluorite to make slag, the application is researched of different slag - making agent such as machine sintering tailings, bauxite, ladle slag. And such materials replace successfully the traditional fluorite to form a economic and reasonable slag making process in steelmaking with semi steel, improve slag melting cffect.
Key Words; steelmaking with semi steel; ladle slag; bauxite; machine sintering tailings; slag making
0
引言
含钒铁水冶金过程中，为提取铁水中的钒元素，
一般采用双联工艺，即铁水经提钒后，用半钢炼钢。由于半钢中硅、锰等元素含量痕迹，因此在炼钢过程中炉渣SiO,、TiO，等酸性氧化物含量很少，致使炉渣组分单一、碱度高、黏度大、流动性差，造成化渣时间长，化渣效果不佳，脱磷效果不好，渣料消耗升高，也限制了溅渣护炉效果及炉龄的提高。目前，为改善半钢炼钢化渣效果，主要使用董石进行造渣，但使用萤石造渣存在着对转炉炉衬侵蚀严重、溅渣效果
收稿日期：201610-10
作者简介：何凯（1975-），男，工程师，2004年毕业于蒸山大学工业电气及其自动化专业，现在河销集团承钢公司从事生产管理工作，
E mail;hekai133.com 万方数据
不良等一系列间题。同时随着董石资源的日益枯竭，价格昂贵，增加了炼钢成本。为此，从改善半钢炼钢效果及降低生产成本的角度出发，通过研究不同造渣剂在转炉半钢炼钢中的应用，进面替代传统的萤石化渣工艺，得到经济合理的半钢炼钢造渣工艺，提高半钢炼钢化渣效果，缩短化渣时间。
半钢炼钢现状分析
1.1
铁水、半钢的化学成分
承钢铁水、半钢的化学成分如表1所示。