100t转炉半钢炼钢复吹工艺优化
何
凯
（河钢集团承钢公司，河北承德067002）
Total No.252 2016,Number12
摘要：针对承钢公司100t转炉原有顶吹及底吹供气元件存在的问题，确定了从顶吹及底吹两方面进行系统优化的思路。主要改进措施有：将原4孔氧枪喷头改进为5孔，应用单环缝式底吹枪代替原来的毛
细管式透气砖，100t转炉的多项经济技术指标得到了改善，大幅度提高了复吹转炉的冶金效果。关键词：转炉；半钢炼钢；复吹工艺：优化
中图分类号：TF703
文献标识码：B
doi:10. 13630/j. cnki. 13 1172. 2016. 1204
文章编号：10065008(2016)12001405
OPTIMIZATIONOFTOPAND
BOTTOMCOMBINEDBLOWNSTEELMAKING
PROCESSWITHSEMI-STEELFOR1OOtCONVERTER
HeKai
(Hesteel Group Chengsteel Company, Chengde, Hebei, 067002)
Abstract: A idea to optimize systematically from top and bottom blown is settled down to solve the problems in the original gas feeding components of 100 ton converter of Cheng Steel. The main improving measures s us n o a o ae a ana o a ao [ao bottom blown lance to substitute the original capillary tubes gas permeable brick. The many economic and technical indexes of the converter are improved, the metallurgical effect of combined blown converter im-proved to a great extent.
Key Words: converter; steel making with semi steel; top and bottom blown process; optimization
引言
作为转炉炼钢的重大技术进步之，复吹转炉
炼钢工艺在全世界范围内得到了飞速发展。由于复吹转炉具备吹炼平稳、化渣快、不易喷溅、钢水氧化性相对较低、废钢比较高等优势，目前国内外绝大多数转炉均采用顶底复吹炼钢工艺]。在转炉复吹工艺中，供气元件是最关键的设备，其中顶吹供气系统中氧枪喷头是影响转炉吹炼过程的核心元件，氧枪喷头的参数设计直接影响冶金性能。底吹供气系统中底吹枪或透气砖的优劣对吹炼过程也起着十分重要的作用，要提高转炉的复吹效果，必须使氧枪喷头及底吹枪或透气砖的各项工艺技术参数设计达到最优化。
收稿日期：2016-10-10
作者简介：何凯（1975－），男，工程师，2004年毕业于蒸山大学工业电气及其自动化专业，现在河钢集团承钢公司从事生产管理工作，E
mail ; hekai133@ 163, com 14
万方数据
转炉复吹现状及存在问题
承钢公司100转炉系统共有100t转炉3座，其中提钒转炉1座，炼钢转炉2座，均采用复吹冶炼工艺。
1.1
氧枪喷头
100t炼钢转炉氧枪喷头采用4孔铸造型，氧枪
操作为变压变枪模式，氧枪喷头的主要工艺参数如表1所示。
表！
Tab. 1
氧枪喷头的工艺参数
Process parameters of nozzle of oxygen lance
氧枪总长氟枪直径
/m 18
/mm 245
马赫数 1.96
氧孔孔数喉口直径出口直径夹角
孔 4
/mm 37.5
/mm 47.9
/e 12
承钢公司采用双联工艺生产，即提钒+半钢炼钢工艺。由于半钢中硅、锰含量为痕迹，造成吹炼过程中酸性成渣物质少，渣系组元单一，并且热量不足，使得半钢炼钢比铁水化渣更加困难，吹炼过程更