摘要：介绍了河钢集团宣钢公司H08A焊条钢生产流程，分析了不同工位时钢中显微夹杂物的粒径分布、数量变化规律，以及铸坏中大型夹杂物的含量、形貌与组成。研究了钙处理前后夹杂物的形貌与组
成，找出了制约产品质量提升的关键环节，对生产具有指导意义。关键词：H08A钢显微夹杂；大型夹杂；粒径分布；变化规律
中图分类号：TG142.1
文献标识码：A
doi;10. 13630/j. cnki. 13 1172. 2016. 0502
文章编号：10065008(2016)050006-04
RESEARCHABOUTINCLLUSIONCHANGE
PATTERNINPRODUCTIONOFHO8AWELDINGRODSTEEL
Jia Jianming
(No.2 Steel Rolling Mill, Hesteel Group Xuansteel Company, Xuanhua, Hebei, 075100)
Abstract: It is introduced the process of Ho8A welding rod steel in Xuanhua Company, analyzed particle diameterdistribution and quantity change patterm of micro inclusion in steel in different work location, and the content, morphology and composition of large scale inclusion in casting blank, researched the morphology and composition of inclusion before and after calcium treatment, got the key links to restrict the products quality improvement.
Key Words; micro inclusion in H08A steel; large scale inclusion; particle diameter distribution; change pattem
引言
钢中的夹杂物破坏了钢的连续性和致密性，对
金属制品的质量有着极为严重的影响(1,2]。由于非金属夹杂物的存在，破坏了钢材集体的连续性，进而降低其理化性能，导致钢材在轧制过程中产生空和微裂纹。对于H08A用钢，由于其是低碳低硅铝镇静钢，夹杂物的种类与数量多少，将会是大包水口结瘤，线材表面产生裂纹、折叠、结疤等缺陷的直接原因。
河钢宣钢生产的牌号为H08A的焊条用钢品质较高，一直以来广受下游用户青。为进一步提升产品质量，了解H08A生产流程中各工位的钢水洁
收稿日期：2016-01-19
作者简介：贾建明（1972－），男，工程师，2015年毕业于河北联合大学钢铁冶金专业，现在河钢集团宣例公司二钢轧厂从事炼钢工艺优
化与技术创新工作，Email;wangzheweigu@163.com 6
万方数据
净度变化情况，有必要对各工位钢中夹杂物种类与含量变化做系统研究。
工艺流程
河钢集团宣钢公司二钢轧厂炼钢车间生产 H08A时采用的生产流程：折罐间→脱硫站→+150t BOF转炉→氢站精炼+连铸→高线轧制。
研究内客及方法
取正常生产的1炉钢作为研究对象，统计各工位不同尺寸的球形显微夹杂和不规则显微夹杂的数量；不同工位夹杂物的粒径分布规律。使用扫描电镜研究氩站处理前后显微夹杂物的形貌与成分。采用大样电解法研究铸坏中大型夹杂物的粒径分布、形貌与成分。
3
研究结果
各工位显微夹杂物的粒径分布与数量变化
3.1
取氢前样、氩中样、氩后样、中间包样、铸坏样，