钒钛矿大高炉开炉顺利达产实践
朱建秋
Total No. 261 2017,Number9
（河钢集团承钢公司炼铁事业部，河北承德067002）
摘要：详细介绍了2500m高炉开炉达产的具体过程，总结了开炉达产的操作经验。在开炉过程中通过优化开炉料和开炉操作制度，在开炉第4天利用系数达到2.19V（m'·d）以上，实现了顺利开炉、快速达产的目标。
关键调：高炉；开炉；达产中图分类号：TF542
文献标识码：B
doi;10. 13630/j. cnki. 13 1172. 2017. 0914
文章编号：10065008(2017)09 005205
PRACTICEOFBLOW-ONAND
SMOOTHLYREACHINGTARGETOUTPUT
OFLARGEVANADIUMTITANO-MAGNETITEBF
Zhu Jianqiu
( Iron Making Division, HBIS Chengsteel Company, Chengde, Hebei. 067002)
Abstract; This paper introduces the specific process of 2 500 m’ BF blowing in and reaching design capacity, summarizes the operation experience of blow - in. By improving the blow - on charge and operation system, the utilization coefficient has been large than 2. 19 /(m' · d) at the fourth day, and the
goal of smooth blow in and fast reaching production has been achieved. Key Words; blast furnace; blow in; reaching target output
0
引言
承钢炼铁事业部某高炉（炉容2500m"）从
2015年9月停炉降料面至风口带，更换破损的铜冷却壁、气密箱、布料溜槽及十字测温装置，检修后炉内采用湿法喷注造衬新技术重新喷涂造衬。2015 年9月30日0：40点火送风，10月3日17：00全风，当日产铁5477.54t.实现了达产目标。本次开炉达产用时4天，实现了顺利快速达产的预期目标。
1
开炉前准备
1.1送风前准备工作
风口、铁口处理
1.1.11
(1)装好送风装置，空压风或氮气等动力介质
恢复输送后，各风门试压，发现跑风及时处理：收稿日期：201705-22
作者简介：朱建秋（1983-），男，工程师，2007年毕业于河北科技大学冶金工.程专业，现在河钢集团承钢公司炼铁事业部T.作，E-mail：
xx_lt_zhujqe edvt. eom. cn 52
万方数据
(2)炉前用铁锹、大锤、氧气管、氧气带、倒靶水管、拆卸风口工具、沙子、炮泥等物资材料要齐全。
(3)各主沟、渣铁沟浇注、捣打、烘烤完毕，用于开炉出铁的大沟先捣打成非储铁式大沟，捣打料厚度根据现场情况而定，两侧及下渣沟用河沙铺好。 1.1.2试车准备
风、水、电、气动力介质供给正常；高炉各系统及设备正常。
1.1.3
物料准备
开炉过程中所用物料准备充足。球团为70% 双福镁球+30%信通镁球：焦炭为100%水熄焦；机烧为100%1#机普烧。
原、燃料的化学性质如表1、表2所示。焦炭灰分的成分如表3所示。