总第262期 2017年第10期
河北冶金 HEBEI METALLURGY
HC420LAD+Z低合金
高强钢镀锌板腐蚀行为研究
刘靖宝，夏明生，杜明山，李勃
（河钢集团唐钢公司技术中心，河北唐山063016）
Total No. 262 2017,Number10
捕要：研究了沉降量、腐蚀时间对HC420LAD+Z低合金高强钢镀锌板失重速率和腐蚀行为的影响。试验表明，在不同的沉降量下，镀锌板的腐蚀速率不同，随着沉降量的增加失重也增加：随着腐蚀时间增长，腐蚀产物覆盖在镀锌板表面，阻碍了纯锌层与溶液的接触，减缓了腐蚀的进行。通过显微组织观察，腐蚀产物呈雪花状。
关键词：低合金高强钢；镀锌板腐蚀；失重；研究
中图分类号：TG178.1
文献标识码：A
doi;10. 13630/j. cnki. 13 1172. 2017. 1009
文章编号：10065008（2017)10004503
STUDYONCORROSIONBEHAVIOROFLOW-ALLOY HIGH-STRENGTHGALVANIZEDSHEETHC42OLAD+Z
Liu Jingbao, Xia Mingsheng, Du Mingshan, Li Bo
( Technical Center, HBIS Group Tangsteel Company, Tangshan, Heibei, 063016)
Abstract: The effects of settlement and corrosion time on the weight loss rate and corrosion behavior of HC42OLAD + Z low alloy high strength galvanized sheet were investigated. The test shows that the corro sion rate of sheet metal was different under different settlement, and the weight loss increased with the in creasing of settlement; corrosion products were covered on the galvanized sheet surface with increasing corro sion time, which hindered the contact between pure zinc layer and solution, and slows down the corrosion Through the microstructure observation, the corrosion product is snowflake shape.
Key Words: low alloy high strength steel; galvanized sheet corrosion; weight loss; study
0
引言
唐钢高强汽车板公司设计生产规模为180万t/ 年（含二期），产品定位为汽车板、汽车用高强钢和超高强钢板、家电板及特殊性能用板，其中低合金高强钢系列是冷轧和镀锌重要的拳头产品，也是盈利的关键。目前镀锌产线低合金高强系列主要包括 HC260~420LAD+Z(1-3】。近期，镀锌低合金高强钢的产量逐月增加，在储存过程中镀锌板表面产生不同程度的锈蚀。因此，需要从机理方面对低合金高强钢的耐蚀性进行研究。
1
试验材料及方法
镀锌板耐蚀试验主要包括两大类：一类是模拟
收稿日期：2017-07-05
作者简介：刘靖宝（1983－），男，博土，2016年毕业于北京科技大学材料科学与工程专业，现在河钢唐钢技术中心从事汽车、家电板研发 I作,E mail;liu_jing_bao@ 163.com
万方数据
腐蚀环境试验检验，如盐雾试验、老化试验、潮湿试验等；另一种试验为自然环境腐蚀试验，如各国在不同气候和地理环境的典型大气试验站进行的挂片试验。
试验材料采用厚度1.5mm的HC420LAD+Z 镀锌板，其化学成分（wt%）为：0.8C，1.2Mn， 0.05Nb,0.03Ti,其余为Fe。经过转炉熔炼后，进行连铸、热轧、酸轧、连续热镀锌。锌层重量双面三点平均值为100g/m，无钝化涂油。
将样品钢板用保鲜膜包裘起来，防止被带钢划
伤，再用剪板机切成150mm×100mm的样片，样片数量为9块。将释板四周进行封边处理，称重：进行 24h、48h、72h盐雾腐蚀后，取出样片进行称重，在场发射扫描电镜上对腐蚀产物进行分析。最后，将封边重量减去腐蚀后重量，即为失重的重量。
45