16MnR钢腐蚀的原因及防护措施
章小芳
（中钢石家庄工程设计研究院有限公司，河北石家庄050021）
Total No. 260 2017,Number8
摘要：分析了锂基润滑脂接触器16MnR钢腐蚀的原因，采用SEM和EDS方法对接触器表面缺陷试样进行分析。结果表明，材料本身、环烷酸、温度、流体流速、冲刷角度等均是导致16MnR钢腐蚀的原因，
从合理选材、降低流速、覆盖防腐蚀层、化学和电化学保护、减少环烷酸腐蚀等方面提出了防范措施。关键词：16MnR钢；腐蚀；原因；措施
中图分类号：TG142.41
文献标识码：B
doi : 10. 13630/j. cnki. 13 1172.2017. 0818
文章编号：10065008（2017)08006203
CAUSESANDPROTECTIVE
MEASURESOF16MNRSTEELCORROSION
Zhang Xiaofang
(Zhongsteel Shijiazhuang Engineering Design Institute Co. ,Ltd. , Shijiazhuang, Hebei, 050021)
Abstract : The reason for the corrosion of the lithium base grease contactor of 16MnR steel was analyzed. The surface defects samples of the contactor were analyzed by SEM and EDS method, and the results showed that the corrosion of 16MnR steel was related with the material itself, naphthenic acid, temperature, flow rate and scour angle. The preventive measures had been taken in the reasonable material selection, the flow rate re-duction, covering anticorrosion layer, chemical and electrochemical protection and the naphthenic acid corro sion reduction, etc
Key Words : 16MnR steel; corrosion; causes; measures
0
引言
冲刷腐蚀又称为磨损腐蚀，是金属表面与腐蚀
流体之间电于高速相对运动而引起的金属损坏现象，也是材料受冲刷和腐蚀交互作用的结果，其危害性较大的局部腐蚀在工业生产领域广泛存在。暴露在运动流体中的所有类型设备，如料浆输送管道泵的过流部件和阀门等，都会遭受到冲刷腐蚀的破坏。针对生产润滑脂16MnR钢接触器产生腐蚀的试样进行分析，找出16MnR钢发生腐蚀的工序及原因，并提出减缓腐蚀的措施
1试验材料和方法 1.1试验材料
取样设备为接触器。接触器是生产锂基润滑脂
的传统设备，有传热速度快、反应时间短的优点。收稿日期：2017-05-10
作者简介：章小芳（1983－），女，工程师，硕士研究生，2010年毕业于北京科技大学材料加工工程专业，现在中钢石家庄工程设计研究院有限公司从事设计工作，E-mail;376114763@qq-com
62
万方数据
接触器在作为通用锂基润滑脂时，接触器的内成分为基础油A、12-羟基硬脂酸、硬脂酸、环烷酸、
氢氧化锂、水。 1.2试验方法
采用SEM观察16MnR钢接触器表面缺陷的形貌和成分，截取部分试样，经磨制后制备成金相试样，在扫描电镜下观察缺陷的形貌。然后，再用 EDS分析不同缺陷部位的成分。结合16MnR钢接触器所处的环境和接触器内生产工艺，找出16MnR 钢出现腐蚀的原因。本试验使用德国徕卡（LEI-CA)公司生产的S440i型扫描电子显微镜，与其搭配的能谱仪为牛津（XOFORD）7060能谱仪。
试验结果与分析
2
2.1试样的形貌和能谱结果
取16MnR钢接触融器发生腐蚀部位的一部分制备金相试样，在扫描电镜下观察，结果见图1。