总第180期 2011年6月
文章编号：1009~9700(2011)03000702
南方金属 SOUTHERNMETALS
Sum.180 June2011
高耐磨贝氏体铸钢衬板生产工艺研究
王振国
（北台钢铁集团有限公司，辽宁本溪117000）
摘要：用Cr-Mn-Si为主加少量其它合金元素的贝氏体铸钢制成衬板，经1080℃正火+200~250℃回火处理组织由贝氏体、铁素体和残余奥氏体组成，其抗拉强度为1600MPa、硬度为（HRC)49、冲击韧性为AKU36J.实验室实
验和生产应用试验表明该材料具有良好的耐磨性能，是衬板材料的理想选择关键词：衬板；正火；回火；贝氏体铸钢；力学性能；耐磨性
中图分类号：TG162.9
文献标识码：A
Astudyoftheproductionprocessforfabricatinglinerplateswith
high wear-resistant bainitic cast steel
WANG Zhen-guo
(Beigang Group, Benxi 117000,Liaoning)
Abstract: A bainitic cast steel containing Cr-Mn-Si as its major alloying elements and other trace elements was developed for fabricating liner plates. The microstructure of the steel normalized at 1080 C followed by tempering at 200 ~ 250 °C was composed of bainite, ferrite and retained austenite, and its tensile strength, hardness and impact toughness were 1 600 MPa, 49 HRC and AKU36J. Cr-Mn-Si steel has excellent wear-resistance and is an ideal candidate for fabricating liner plates.
Key words: liner plate; normalizing; tempering; bainitic cast steel; mechanical properties; wear-resistance
冶金企业大量使用储运物料的漏斗，漏斗内部镶有耐磨的衬板，其在作业过程中直接与铁粉、焦炭、球团等硬质物料接触，条件恶劣，磨损严重，消耗量大，如何提高衬板的抗冲击性、抗磨损性，开发新材料衬板，提高储运系统的工作效率，具有重要的经济意义，
1材料生产工艺 1.1材料化学成分
材料的化学成分见表1.
表1材质成分
元素
碳
备
硅
铬
钼
% 镍
含量 0.25 ~0.35 1.8~2.1 1.4~1.6 0.6~1.0 0.2~0.4 0.1~0.7 1.2生产工艺
新型铸钢衬板采用中频感应电炉冶炼，按常规收稿日期：2010-11-29
铸造，经过1080℃正火+200~250℃回火处理，
2材料的组织和性能 2.1金相组织和力学性能
采用Neophot-3型光学显微镜（OM）观察，显微组织为贝氏体+铁素体+残余奥氏体（见图1）
图1金相组织
作奢简介：王振国（1957-），男，1982年毕业于沈阳机电学院金属材料及热处理专业，工程师，