船板钢奥氏体晶粒浸蚀显示方法的改进
刘金源，郑晓明，廖美华，梁建珠，冯曼君（广东省韶关钢铁集团有限公司，广东韶关512123）
摘要：采用15%盐酸酒精侵蚀显示低含碳量或晶粒不均匀的奥氏体晶粒，往往不能获得良好的效果，直接影响晶
粒度的准确评定.尝试采用1%的氧化高铁盐酸溶液来浸蚀显示奥氏体晶粒，取得了令人满意的效果，关键调：浸蚀显示；奥氏体晶粒；氯化高铁；盐酸酒精
中图分类号：TB115；TC142.1
文献标识码：B
An improvement of the etching technique for displaying
austenitegrainsinhullstructureplatesteel
LIU Jin-yuan, ZHENC Xiao-ming, LIAO Mei-hua, LIANG Jian-zhu, FENG Mang-jun
(Shaoguan Iron & Steel Group Co., Ltd., Shaoguan 512123, Guangdong)
Abstract: It is usually difficult to obtain a good result in showing the low-carbon- or size-uneven austenite grains when a 15% hydrochloric-alcohol solution is used as the etchant, which inevitably affects the grain size measurement of austenite A new etching reagent composed of hydrochloric acid solution containing 1% FeCl3 was therefore employed to etch the aus-tenite grains, and a satisfactory result obtained.
Key words: etching; austenite grain; FeCl3; hydrochloric-alcohol solution
0前言
晶粒度是表示晶粒大小的一种尺度，晶粒大小对金属材料的机械性能和工艺性能有很大的影响。因此晶粒度的测定广泛应用于材料的开发和产品质量的检测判定.晶粒度的测定包括两个步骤，即晶粒的显示和晶粒尺寸的测定评级.晶粒的显示是晶粒度评定的先行条件，晶粒显示的好坏直接影响到晶粒度评定的准确.《金属平均晶粒测定方法》（CB/ T6394-2002）附录中推荐了气氛氧化法+15%盐酸满精浸蚀作为显示奥氏体晶粒的方法之，这种方法适用碳含量为0.25%~0.60%的碳素钢和合金钢，其原理是将钢处在氧化气氮下加热，因晶界比晶粒内具有更大的化学活性，氧化作用优先在晶粒边界发生而将晶粒大小显示出来.通常的方法是将试样磨抛成一镜面，将抛光面朝上置于空气炉中，加热温度控制在900±10℃，保温时间为90mim，然
收稿日期：2008-0721
后人清水中，试样完全冷却至室温后取出，再轻磨抛试样到一定的光洁度后，用15%盐酸酒精溶液进行浸蚀至晶粒显示清楚为止。
1气氛氧化法+15%盐酸酒精浸蚀法的不足之处
采取气氛氧化法+15%盐酸酒精浸蚀法“对各种钢般能得到较完整的氧化铁网，但在混晶的试样上，则往往出现大片区域无氧化铁网，或者网的形象不规则，不能评定，也可能造成误评"[]，实践经验也表明，15%盐酸酒精浸蚀法不太适合于晶粒不均勾和低碳钢（C%<0.1%）试样.广东省韶关钢铁集团有限公司（以下简称“韶钢”）高强度D级船板在保证强度基础上为提高-20℃低温冲击韧性，在化学成分控制上采取低碳，或添加少量的锯或钒元素，其金相组织特证表现为晶粒大小不均匀并略呈饼状分布的铁素体+珠光体组织（见图1).采取气
作者简介：刘金源（1975-），男，1997年毕业于大连铁道学院工业分析专业，工程师。