韶钢烧结熔剂筛HPM聚氨酯筛板生产试验
张兴强，郭海山"，罗皓，雷建伏，石巍”（1.宝钢集团广东省韶关钢铁有限公司，广东韶关512123： 2.江苏亿亿和华筛分设备有限公司，江苏徐州221004）
摘要：韶钢4、5、6号3台烧结机投产后，烧结用破碎生产熔剂矿消耗量逐年增加，现需求量在55万Va以上，供料车间雨季生产频繁出现弹簧钢丝网黏贴堵筛孔，熔剂筛分遇到极大困难为解决黏贴堵筛孔，开展HPM聚氨酯
筛板现场生产试验，通过试验结论研讨，对于聚氨酯筛板应用于烧结熔剂筛分可行性进行分析论证关键词：烧结熔剂；HPM；筛分效率
中图分类号：TF046.4
文献标识码：B
SieveProductionTest onSinteringFluxHPMPolyurethaneSieveat Shaosteel
ZHANG Xing-qiang, GUO Hai-shan, LUO Hao, LEI Jian-fu, SHI Wei
(1 Baosteel Group Guangdong Shaoguan Iron &Steel Co. ,Ltd. , Shaoguan, Cuangdong, 512123,P. R. China
2. Jiangsu HEWA Sereening Product Co., Ld, Jiangsu,221004, P. R. China)
Abstract; After the Sintering machines 4#, 5#, and 6# at Shaosteel were put into operation, sintering flux consisted of crushed ores increases year by year, its demand now increases to 550,000 tons / year. The spring steel meshes were fre quently blocked in the material supply workshop during raining seasons, it is difficult to sieve the flux. To solve the conges-tion, adhesive blocking sieve, HPM polyurethane is tested on site. The test conclusions are discussed in order to demon
strate and analyze the feasibility of applying the polyurethane sieve in screening the sintering flux Key words: sintering flux; HPM; screening efficiency
0前言
烧结生产需要加入熔剂，其目的有两个：其一是将高炉需要添加的石灰石、白云石移到烧结过程中，使高炉中的部分化学反应在烧结过程中进行，从而起到提高高炉冶炼强度和降低焦比的作用；其二是熔剂中的CaO和MgO与烧结料中铁的氧化物和酸性脉石在高温作用下，生成一种还原性好的低熔点化合物，使烧结料在燃烧消耗较少的情况下，获得足够的液相，改善烧结矿强度和冶金性能.宝钢集团广东省韶关钢铁有限公司（以下简称“韶钢”）炼铁厂烧结生产熔剂消耗量在55万Va以上，雨季熔剂破
收稿日期：2014-0729
碎生产过程中，熔剂筛子容易堵塞、黏贴堵筛孔，造成筛分效率较低，熔剂破碎产量低，无法满足烧结熔
剂成品供料的需求， 1工艺流程
石灰石、白云石入厂粒度均为10~40mm，最大粒度为60mm，其中粒度小于10mm与大于40mm 部分所占比例之和不得大于10%.而烧结工艺要求熔剂粒度小于3mm部分应大于90%，为了保证粒度符合要求，烧结熔剂破碎工艺流程采用闭路破碎筛分流程，即块状熔剂经过破碎机以后，还要经过筛分设备，筛下物（3mm）为成品，送烧结配料室参
作者简介：张兴强（1962-），男，1988年毕业于中南工业大学机械工程专业，工程师，