总第205期 2015年8月
文章编号：1009-9700(2015)04004704
南方金属 SOUTHERN METALS
冷轧析出强化钢拉伸应变痕
产生机理及影响因素
田中青
（宝山钢铁股份有限公司，上海201900）
Sum.205 August2015
摘要：概述了冷轧析出强化钢拉伸应变痕对产品使用的影响，分析了此缺陷的产生机理，指出成品的届服延伸率大小直接影响拉伸应变衰的严重程度；从一贯制工艺角度出发，分析了热轧卷取温度、冷轧退火温度、平整率及平
整轧制力等工艺参数对成品拉伸应变衰的影响，提出了改进方向关键调：析出强化钢拉伸应变衰；一贯制工艺
中图分类号：TG335.11
文献标识码：A
MechanismofProductionandInfluencingFactorsofTension Strain
TraceofCold-rolledPrecipitationStrengthSteel
TIAN Zhong-qing
(Baosteel Co. Ltd. Shanghai 201900, P. R. China)
Abstract: The effects of tension strain trace of cold-rolled precipitation strength steel on the users was summarized. Mecha nism of this defect has been analyzed. On the base of consistent process,the effects of hot rolling temperature, cold annea ling temperature, temper rolling rate and temper rolling force on the tension strain trace of cold-rolled precipitation strength steel have been analyzed, and the improvement direction has been given
Key words: precipitation strength steel; tension strain trace; consistent procese 0引言
析出强化是金属材料常用的强化方式之一，析出强化钢是通过在钢基体中添加一定量的Nb、Ti等合金元素，在随后的热轧、冷轧过程中以NbC或TiC
的形式析出，从而达到强化钢基体的目的
冷轧析出强化钢具有较高的强度，良好的成型性和表面质量，被广泛用于汽车生产行业，生产汽车的结构件、安全件等.析出强化钢产品在加工成零件后，表面会出现树枝状的条纹，条纹与材料轧制方向呈一定角度，严重的甚至有高低起伏的手感，一般称此缺陷为“滑移线”，即所谓的拉伸应变银，缺陷典
型形貌如图1、图2所示收稿日期：2015-02-06
图1汽车零件滑移线“形貌图2汽车零件“滑移线”形貌
作者简介：田中青（1980-），男，2006年重庆大学材料科学与工程专业硕士研究生毕业，工程师