总第193期 2013年8月
文章编号：10099700(2013)04002004
南方金属 SOUTHERN METALS
Sum.193 August2013
韶钢6号高炉炉缸侧壁温度升高的治理
卢永凯，郭海山，聂红卫
（宝钢集团广东韶关钢铁有限公司，广东韶关512123）
摘要：韶钢6号高炉大修投产后炉缸温度逐步升高，炉缸碳砖温度最高达800℃，个别冷却壁水温差及热流强度超标.本文对炉缸冷却壁水温差偏高及侧壁温度上升原因进行了分析，通过强化冷却、采取炉缸压浆，适当抑制边缘气流，合理调整风口布局等综合治理措施，炉缸冷却壁水温差及侧壁温度逐步下降并趋于稳定，为治理高炉侧壁温度升高积累经验
关键调：水温差；热流强度；灌浆
中图分类号：TF065
文献标识码：B
ControlofBFHearthSideWallTemperatureRisingatSGIS
LU Yong-kai, GUO Hai-shan, NIE Hong-wei
( Baosteel Group Guangdong Shaoguan Iron & Steel Co. , Lid. , Qujiang, Guangdong, 512123,P. R. China)
Abstract: After the overhaul of No. 6 BF at SGIS, the hearth temperature gradually was rising, the temperature of carbon bricks reached up to 800C , walter temperature difference and thermal flux intensity of some cooling walls exceeded the standard. This paper shows the reasons why the cooling water temperature of hearth cooling walls rises so high. The cooling water temperature of hearth cooling walls and wall temperature are gradually decreased and kept stable by strengthening the cooling, having the hearth pressure grouted, properly restraining the edge flow, reasonably adjusting the tuyere layout and adopting other measures, and the experience for solving problems of side wall temperature rising for BF has been aceumula-ted.
Key words: temperature difference; heat flux intensity; grouting
0概述
宝钢集团广东韶关钢铁有限公司（以下简称“韶钢")6号高炉有效容积750m，2011年3月停炉大修，这次大修为了节约成本，尽量利用旧设备，设一个铁口，大沟改成储铁式铁钩；上代炉龄设一个渣口，这次大修单独做个冷却盘封住，取消渣口；设 18个风口；冷却系统大部分使用上一代的旧冷却壁，只对损坏的进行更换，1-4段采用光面双层冷却壁，5-6层采用镶砖双层冷却壁，再往上是20层铜冷却板，7-8层是铸铁冷却壁，最上方是炉喉水冷钢砖，全炉体采用工业水开路循环冷却；炉顶装料设备采用串罐式无料钟炉顶、料车式上料，炉顶煤气余压发电（TRT），十字测温装置，都是全部利旧；只
收稿日期：2013-01-24
有炉底和炉缸全部重新更换，采用国产大块碳砖+
陶瓷杯的综合水冷炉底， 16号高炉的现状
韶钢6号高炉2011年9月12日开炉，开炉后炉缸侧壁温度不断升高，2011年11月16日因市场不好进行满料线封炉停炉，封炉半年后于2012年4 月28日重新点火开炉，开炉后半个月炉缸侧壁温度不断上升，炉缸水温差和热流强度上升到预警水平，铁口漏煤气很大，而且有较大冲力，铁口区域水温差和热流强度更为明显，到8月份最高测温点已经上升到847℃，位于铁口下方
水温差和热流强度也明显上升，水温差最高是 3层3号达到1.7℃，3层1号热流强度达到11106
作者简介：户永凯(1973-），男，1996年毕业于重庆钢铁专科学校炼铁专业，工程师，