总第202期 2015年2月
文章编号：10099700(2015)01003703
南方金属 SOUTHERN METALS
高炉煤气喷雾冷却工艺在韶钢煤气柜作业区的首次应用
戴金华，危中良，文坚
（宝钢集团广东韶关钢铁有限公司，广东韶关512123）
Sum.202 February 2015
摘要：介绍韶钢煤气柜作业区高炉煤气的冷却工艺应用情况，通过比较两种冷却工艺的优缺点，指出节能降耗型
的高炉煤气冷却工艺是今后煤气柜作业区高炉煤气冷却工艺的发展方向，值得在钢铁企业大力推广运用关键词：高炉煤气；喷雾冷却；煤气柜
中图分类号：TQ547.9*1
文献标识码：B
TheFirstTimeApplicationofSprayCoolingforBFGasTankAreasatSGIS
DAI Jin-hua, WEI Zhong-liang,WEN Jian
(Baosteel Group Guangdong Shaoguan Iron&Steel Co. ,Ltd, ,Shaoguan, Guangdong, 512123,,P. R. China)
Abstract: This paper introduces the application of the BF gas cooling technology for the BF gas tank areas. Through com paring the advantages and disadvantages of two kinds of cooling processes, it points out that the energy saving type of BF gas cooling process in the gas tank areas will be the direction in future, which is worth of being popularized in the iron and steel enterprises vigorously
Key words; blast furmace gas; spray cooling; gas tank
工业企业在利用高炉煤气时，为保证高炉煤气加压风机和干式煤气柜的运行性能稳定，在进人干式煤气柜和煤气加压风机之前，必须控制煤气温度在60℃以下.由于宝钢集团广东韶关钢铁有限公司（以下简称“韶钢”）高炉煤气除尘采用全干法布袋除尘，经干法布袋除尘后的高炉煤气温度为80~ 200C，因此对高炉煤气进行加压和利用十式煤气柜调节高炉煤气管网之前，必须对高炉煤气进行降温，使高炉煤气的温度符合煤气加压机和干式煤气柜的工艺运行要求.
韶钢四柜区煤气柜工程于2008年立项，2010 年作为轧钢的配套项目进行实施.项目主要包括一套20万m/h的高炉煤气加压系统，该系统采用了先进的全自动控制喷雾冷却工艺取代韶钢原湿式喷淋工艺.项自于2010年动工，2011年5月建成投产，喷雾冷却工艺作为韶钢煤气加压系统的首次应
收稿日期：2014-08-14
用，运行至今，充分展示出降温效果好、运行费用低等优点，有显著的经济效益和社会、环保效益
1煤气柜作业区高炉煤气冷却工艺应用情况
目前，国内应用比较普遍的煤气柜作业区高炉煤气冷却工艺有两种：一种是喷淋式冷却工艺，另一种是喷雾冷却工艺，
1.1喷淋式冷却工艺
喷淋式冷却工艺采取气液逆流方式接触，即冷却水与高炉煤气逆向流动，冷却水带走煤气显热，从而达到煤气降温的目的
1999年，全国首座新型（POC型）干式高炉煤气柜在韶钢二柜区建成投产，并配以喷淋式冷却工艺，该柜区高炉煤气冷却工艺见图1.
作简介：戴会华（1987－），男,2011年毕业于辽宁科技大学化学工程与工艺专业，助理工程师