负极添加剂对铅酸电池低温性能的影响
黄镇，王殿龙，尚晓丽
（1.哈尔滨工业大学化工学院，黑龙江哈尔滨150001； 2.浙江南都电源动力股份有限公司，浙江杭州311305）
摘要：本文研究了负极添加剂木素、离殖酸、硫酸领、炭黑对铅酸蓄电池低温性能的影响。结果表明，提高腐殖酸和硫酸领的添加量，能够提高铬酸蓄电池的低温容量及低温大电流放电性能，但在一定程度上会降低电池的充电接受能力。
关键词：负极添加剂；木素磺酸钠；离殖酸；硫酸领；炭黑；低温容量；铅酸蓄电池；充电楼受；大电流放电
中图分类号：TM912.9
文献标识码：B
文章编号：1006-0847(2017)01-23-04
EffectsofNAMadditivesonlowtemperatureperformanceof
lead-acidbatteries
HUANG Bin'2, WANG Dianlong', SHANG Xiaoli?
(I. School of Chemical Engineering, Harbin Institute of Technology, Harbin Heilongjiang 15000I; 2.Zhejiang Narada Power Source Co., Litd., Hangzhou Zhejiang 3I1305, China)
Abstract: The effects of sodium lignosulphonate, humid acid, barium sulfate and carbon black as NAM additives on the low temperature performance of lead-acid batteries are investigated. The results show that discharge capacity and high-rate discharging performance at low temperature is significantly improved by increasing the doping level of humid acid and barium sulfate. However, the charge acceptance is reduced at the same time
Keywords: NAM additives; sodium lignosulphonate; humid acid; barium sulfate; carbon black low temperature capacity; lead-acid battery; charge acceptance; high-rate discharging
0前言
近年来，以铅酸蓄电池为动力的短途低速纯电动车作为一种代步工具，具有价格便宜、使用方便、节能环保等多种优势，已逐渐被人们接受和使用。目前，短途纯电动乘用车市场主要集中在山东、河北、江苏、浙江等地，而东北、西北等市场
收稿日期：2016-06-29
万方数据
销量不佳，主要是因为铅酸蓄电池在低温条件下性能下降，表现为充电困难、续航里程缩短。
铅酸蓄电池的低温性能主要取决于负极板。在低温条件下，负极板的主要失效模式是钝化和收缩。在负极活性物质中加入适当添加剂是主要的解决手段之一。负极配方中的硫酸锁、炭黑等无机物和木素、腐殖酸等有机膨胀剂的作用机理主要有：硫酸钡可以作为电池放电时硫酸铅的成核剂，降低硫酸铅的过饱和度，抑制硫酸铅沉淀生成致密的不可渗透的钝化膜"；炭黑或者乙炔黑的主要功能是导电2-4，木素、木素磺酸盐、腐殖酸等有机物可以