不同配比下粉煤灰热再生沥青胶浆路用性能评价研究
Study on Performance Evaluation of Fly Ash Heat Recycled Asphalt Mortar with Different Proportioning
张军
（西安铁路职业技术学院，陕西西安710600）
摘要：为了研究粉煤灰含量对混合料的影响，本文首先设计了粉煤灰沥青混合料试验组。然后，采用车辙试验，劈裂试验，浸水马歌尔试验和冻融旁裂残余强度试验的方法，对粉煤灰热再生沥青混合料的高温性能，低温性能和水稳定性进行测定研究，为粉煤灰工程应用研究提供理论依据。
关键词：粉煤灰；高温性能；低温性能；水稳定性
中图分类号：U416.25
文献标识码：A
文章编号：1005-8249（2018）04-0084-03 Zhang Jun
(Xi'an Railway Vocational & Technical Institute, Xi'an 710600, China)
Abstract: To study the effeet of fly ash on the mixture, the heatrecycled asphalt mixture of fly ash was designed. The high temperature performance, lowtemperature perfomance and water stability of fly ash heat reeycled asphalt mixture were studied by rutting test, splitting test, soaking Marshall Test and freezethaw splitting residual strength experiment. It provides the theoretical basis for the engineering application research of fly ash.
Keywords: fly ash; high ttemperature performance; low temperature perfomance; water stability
公路建设是粉煤灰应用的主要途径之一，粉煤
灰沥青胶浆性能的发挥要以沥青混合料为载体，通过沥青混合料的路用性能体现沥青胶浆的性能【12]因此，优良的混合料路用性能是粉煤灰厂拌热再生沥青混合料应用的基本前提。本文以粉煤灰掺杂沥青研究为背景，探究不同配比下的粉煤灰热再生沥青胶浆的路用性能【1.2】
试验材料 1
（1）粉煤灰选取云南低钙粉煤灰作为研究对象，制备AC-16型沥青混合料【3]
（2）沥青以昆仑牌90号国产沥青路面为基质沥青，具体的测试结果如表1所示。通过表1，可以看出沥青各项数据符合使用规范要求。可以通过此种沥青进行试验探究。
作者简介：张军，（1983－），男，讲师，工程硕士（建筑与土木工程）
收稿日期：2018-05-28
·84 · 万方数据
表1沥青各项性能
试验项目
针人度（25℃，100g，5s）/0.1mm
延度（5em/min，25℃）/em
软化点/℃ 闪点℃ 含蜡量/%
密度（15℃）/（g/em’)
试验组设计 2
90号沥青 94.5 133.1 49.5 263 2.8 0.976
试验方法 T0604 T0605 T0606 T0611 T0615 T0603
本文选取的掺粉煤灰热再生沥青的类型为AC-16，采用确定的混合料级配组成制备粉煤灰沥青混合料试件，然后以0，40%，70%和100%的粉煤灰代替矿粉作为对照变量进行试验。通过车辙试验，劈裂试验，浸泡马歌尔试验和冻融劈裂残余强度试验，探讨了沥
青混合料的高温性能，低温性能和水稳定性的变化。 3试验方法及结果分析
3.1粉煤灰对混合料高温性能影响分析