粉煤灰综合利用
FLYASHCOMPREHENSIVEUTILIZATION 锂渣复合粉煤灰高性能混凝土早期抗压强度影响因素的比较分析
The Comparative Analysis of Influence on the
2012NO.1 专题研究
Early Compressive strength of lithium Slag Compound Fly Ash High Performance Concrete
周海雷，杨恒阳，努尔开力·依孜特罗甫，侍克斌
（新疆农业大学水利与土木工程学院，乌鲁木齐830052）
摘要：运用正交试验设计的方法配制锂渣复合粉煤灰高性能混凝土，运用极差分析和方差分析的方法分析了水胶比、锂渣掺量和粉煤灰掺量对锂渣复合粉煤灰高性能混凝土的早期抗压强度的影喇，得出锂渣较粉煤灰对锂渣复合粉煤灰高性能混凝土早期抗压强度影响显著。在进行极差分析时，引人了极差相对差异度这一概念。
关继询：正交设计试验，早期强度，极差相对差异度
中图分类号：TU528.2
文献标识码：A
文章编号：1005-8249(2012)01-0003-06
Zhou Hai-lei, Yang Heng-yang, Nuerkaili - Yiziteluofu, Shi Ke-bin
(College of Water Conservancy and Civil Engineering, Xinjiang Agricultural University, Urumqi 830052, China)
Abstract; Lithium slag compound fly ash high performance eonerete was made by the orthogonal experiment design method, the preparation of the use of poor analysis and variance analysis method to analyse the impact that the water-binder ratio, lithium slag mix content and the fly ash for lithium slag compound fly ash of high performance conerete ecompressive strength of the early. Lithium slag on lithium slag compound fly ash high performance concrete compressive strength has significance effects Dmng early. Dmng analysis of the poor, poor relative difference degree was introduced the eoncept.
Key words; orthogonal experiment design; early strength; poor relative difference
锂渣是利用锂辉石矿石经过约1200℃高温烧后用硫酸法生产碳酸锂过程中产生的工业废渣，锂渣中有较多的无定形SiOz、Al,O，等，具有较高的火山灰活性"，适合用作混凝土的掺合料。粉煤灰用作混凝土的掺合料，可以发挥其火山灰效应、微集料填充效应、形态效应。本文利用锂渣和粉煤灰复掺，运用方差分析的的方法来探究这两种掺合料对混凝土早期抗强度的影响。
"基金项目：1.国家高等学校博士点专项科研基金资助课题(200807580007) ;
2.新疆水利水电工程重点学科基金资助项目（xjsdxk
20100212)
第一作者：周海营（1987~），男，硕士研究生。从事水工建筑材料研究；
通讯作者：侍克斌（1957~），教授，E-mail；xndsg@sins.com
收稿日期：2011-09-06 万方数据
1材料与方案设计 1.1原材料
(1)新疆天山水泥股份有限公司生产的天山牌 42.5R级普通硅酸盐水泥（技术性质见表1，化学性质见表2）。（2)新疆锂盐厂生产的烘干锂渣，淡黄色，粉状，密度2.48g/cm（化学性质见表2）。（3）玛纳斯电厂生产的Ⅱ级粉煤灰（化学性质见表2，技术性质见表 3）。（4)山西奥鑫建材有限公司生产的萘系高效减水剂。(5)骨料：粗骨料为乌鲁木齐乌拉泊砂石料场的卵石，最大粒径25mm，经水洗后含泥量为0.3%；细骨料为乌拉泊砂石料场的碎石，细度模数2.6，为中砂，经水洗后含泥量为1.2%。