涂装技术
第46卷第5期 2016年5月
涂料工业
PAINT & COATINGS INDUSTRY
Vol.46No.5 May2016
施工工艺参数对水性汽车铝粉漆颜色和外观的影响
张立军，胡玲，郭书，苏海涛（华晨宝马汽车有限公司，沈阳110000）
摘要：介绍了欧系整车厂中流行的免中涂涂装工艺（IPP），并以水性铝粉漆为例，讨论了各涂层膜厚、色漆闪干时间、预烘烤条件、喷涂参数对颜色和外观的影响，推荐了色漆和清漆的施工膜厚范围，研究了上述施工参数对铝粉定向排列的影响以及水性铝粉漆的颜色和外观特性。
关键词：水性铅粉漆：颜色；外观：膜厚：预烘烤温度：闪干时间；铝粉定向排列
中图分类号：TQ639
文献标识码：A文章编号：0253-4312（2016)05-0070-07
Influence of Application Parameters on Color and Appearance of Waterborne Aluminium Paint
Zhang Lijun,Hu Ling,Guo Shu,Su Haitao(Brilliance BMW Co.,Lid.,Shenyang11000, China)
Abstract:The IPP for European style vehicle is introduced. Taking the waterborne alumi-num paint as example, the effects of film thickness, flash off time, prebaking condition and spraying parameters on color and appearance of the cured film are investigated. Thus, the rec-ommended range of the film thickness of basecoat and clear coat is provided. In addition, some key parameters affecting the aluminum orientation and the appearance and color of the water-bornealuminum paintwere studied.
Key Words:waterborne aluminium paint; color; appearance; thickness; prebaking tem-perature; flash off time; aluminum orientation
随着国家越来越重视环境保护，2012年以后建设的整车厂都采用了低VOC排放、环境友好的水性色漆配套溶剂型罩光清漆涂装技术，其中水性漆溶剂含量只有传统溶剂型涂料的1/10~1/7。目前国内流行的水性汽车漆涂装工艺有3种，即传统水性汽车漆3C2B涂装工艺、3C1B涂装工艺、免中涂涂装工艺。传统水性汽车漆3C2B涂装工艺类似传统溶剂型3C2B涂装工艺，目前很多汽车厂都在应用，如上海通用北盛厂、一汽大众奥迪新厂都使用了该工艺： 3C1B涂装工艺主要由日系的涂料供应商关西和立邦公司研发，主要用于日系汽车工厂：免中涂涂装工艺在不同涂料厂商的叫法及具体工艺有所不同，在
PPG称免中涂装工艺为B1B2，巴斯夫称为IPP，艾仕德称为Eco-concept。该工艺在电泳之后直接喷涂色漆，取消了中涂层2，但也造成一定程度的施工困难，对电泳粗糙度要求变高。IPP涂装工艺由BASF 和PPC等国外涂料供应商研发，类似于溶剂型3C1B 涂装工艺，该工艺降低了能源消耗和人力成本3），对颜色和外观的控制相对简单，目前国内大部分欧系整车厂采用IPP水性漆涂装技术。
IPP工艺简介
华晨宝马涂装车间采用IPP工艺，色漆分为
作者简介：张立军（1982一），男，硕士，工程师，主要从事水性漆喷涂参数研究。 02