应用研究
第43卷第5期 2013年5月
不工修
PAINT & COATINGS INDUSTRY
FEVE涂层的老化与服役寿命预测研究
张晓东，赵铖，郭燕芬，王俊，揭敢新，黄海军
Vol.43No.5 May2013
（中国电器科学研究院有限公司，工业产品环境适应性国家重点实验室，广州510663）摘要：利用氙灯老化试验研究了FEVE氟碳涂料的光泽、颜色变化规律，通过金相显微镜和 ATR-FTIR考察了涂层表面形貌和分子结构的变化，结果表明：FEVE树脂的薄弱环节为酯基。根据环境应力量化模型预测了涂层在海南湿热环境中的服役寿命。
关键词：FEVE氟碳涂料：氙灯老化试验：环境应力量化模型：服役寿命预测中图分类号：TQ630.7*2-
文献标识码：A文章编号：0253-4312(2013)05-0062-04
Study on Aging and Service Life Prediction of FEVE Coating Zhang Xiaodong,Zhao Yue,Guo Yanfen,Wang Jun,Jie Ganxin,Huang Haijun(State Key Laboratory of Enxironmental Adaptabilityfor Industrial Products,China National
Electric ApparatusResearchInstituteLad.,Guangzhou510663,China)
Abstract:In this article, the change of gloss and color of FEVE fluorocarbon coating has been studied in xenonlamp weatherometer,and by use of metallographic microscope andATR-FTIR, the surface morphology and molecular structure of the coating has also been investi-gated. The results showed that the ester group is the weakest part in FEVE resin.Finally, FEVE service life of the coating in Hainan dampheat environment was predicted by environ-ment stress quantitative model.
KeyWords:FEVEfluorocarboncoating;xenonlampweatheringtest;environmentstress quantitative model;service life prediction
FEVE氟碳涂料以其良好的施工性能、优异的耐久性、耐化学性等，在建筑外墙、钢结构重防腐及新能源等领域获得越来越广泛的应用。理论上，结构规整的FEVE树脂具有优异的耐候性，但实际使用中，由于FEVE氟碳涂料与其他组分的相容性以及颜料的选择等因素，会降低其耐候性。如何通过人工加速老化试验去验证FEVE涂料是否达到供应商所保证的长寿命，是人们非常关心的一个问题。
本研究根据环境应力量化模型，利用氙灯加速老化试验研究了某FEVE涂料的耐老化性能，并对其在湿热自然环境中的服役寿命进行了预测。
1实验部分
涂层配套体系
1.1
涂层样板：140mm×70mm，客户提供涂层配套
体系：铜金底漆+FEVE罩光清漆 1.2灯老化试验
依据GB/T1865—2009（色漆和清漆人工气候老化和人工辐射暴露（滤过的氙弧辐射）》进行氙灯老化试验，试验参数如表1所示。氙灯老化试验箱为 AtlasCi4000型，将样品用夹具固定后挂在旋转的试
作者简介：张晚东（1978一），男，工程师，主要研究高分予材料的老化与防护。 62