紫外光固化阴极电泳涂料的研究
陈兴兰，陈卫东，顾丽萍，凌晓飞，周志成
（中海油常州涂料化工研究院，江苏常州213016）
Vol.43No.9 Sep.2013
摘要：制备了以环氧为主体的UV固化阴极电泳涂料，用FT-IR对产物结构进行了表征：同时研究了电泳时间、电泳电压、闪蒸条件、固化时间等对涂膜的影响，得到合适的施工条件：电泳时间为 80s，电压为60V.闪蒸温度为80℃，闪蒸时间为10min，固化时间为120~150s。该条件下，涂膜综合性能优异。
关键词：阴极电泳；光固化：闪蒸条件
中图分类号：TQ637.83
文章编号：0253-4312(2013)09-0052-04
文献标识码：A
Synthesis and Properties of UV-Curable
Cathodic Electrophoretic Coatings
ChenXinglan,Chen Weidong,GuLiping,Ling Xiaofei,Zhou Zhicheng
(CNOOC Changzhou Paint and Coatings Industry Research Institute,ChangzhouJiangsu213016,China) Abstract:The title UV - curable cathodic electrophoretic coating was synthesized with ep-oxy as the main binder.The structure of products were characterized byFT -IR.At the same time, the effects of the electrophoresis time,electrophoresis voltage, flash time and curing time on the flim performance were discussed. The experiment results indicated that the film had better conprehensive properties when the electrophoresis time was 80 s,voltage was 60 V, the flash temperature was 80 C, the flash time was 10 min and the curing time was 120 ~150 s.
Key Words:cathodic electrophoretic coating;UV curing;water solubility
目前阴极电泳涂料涂膜固化方式主要为热固化，固化温度一般为140~180℃.因此许多材料因温度的影响较难进行电泳涂装")。为满足成形加工、金属重复利用及产品材质轻、成本低的要求，锌、铝压铸等材料被在大量使用，而这些产品在电泳涂装的高温条件下，产生的压铸件砂眼巢穴、电镀层脱皮等现象均会影响产品的外观。解决这类问题的方法之一是降低涂料涂装时的固化温度（3)。紫外光固化电泳涂装不需要很高的固化温度，既能满足产品在电泳涂装时的需要，又能解决涂装基材受温度影响的问题3) 有很好的发展前景[4]
本研究合成了紫外光固化阴极电泳涂料的新型树脂，操讨了影响电泳涂装的各种工艺参数，并测试了该涂料的各项性能。结果表明：合成的光固化阴极电泳涂料具有较好的水溶性和较好的贮存稳定性，同
时电泳得到的涂膜平整、光滑，性能优异。 1
实验部分 1.1主要原料