2016年9月
PAINT&COATINGS INDUSTRY
Sep.2016
阴极电泳涂料用泳透力提升助剂的合成及应用
邓力，王琳，王清丹，蔡志强，徐一丁
（上海金力泰化工股份有限公司技术中心，上海201417）
摘要：用甲苯二异氰酸酯（TDI)与改性酚醛树脂合成聚氨酯预聚体，之后引人一定量的N,N-二甲基乙醇胺（DMEA），然后用冰醋酸中和成盐后乳化，得到阴极电泳漆泳透力提升助剂。按一定比例添加至阴极电泳涂料(CED)中可显著提高槽液的泳透力。
关键词：甲苯二异氰酸酯；改性酚醛树脂；泳透力；阴极电泳涂料
中图分类号：TO637
文献标识码：A
文章编号：0253-4312(2016)09-0054-04
Synthesis of Throwing Power Additives andIts Applications in Cathodic Electrodeposition Coatings
Deng Li,Wang Lin, Wang Qingdan, Cai Zhiqiang, Xu Yiding(R&D Center,Shanghai Kinlita Chemical Co.,Lid., Shanghai 201417,China)
Abstract:A prepolymer was prepared from toluene disocyanate（TDI)and modified phe-nolic resin, and then incorporated with N,N-dimethyl ethanolamine (DMEA),further neu tralized with glacial acetic acid, finally emulsified to form an additive for cathodic electrodepo sition coatings. This additive can help enhance the throwing power of bath significantly
Key Words:toluene disocyanate; phenolic resin; throwing power; cathodic electrodepo sition coatings
阴极电泳涂料自20世纪70年代开始发展，已经有超过40a的历史。由于它具有比阳极电泳涂料更优异的防腐蚀性能，涂料利用率高，涂装自动化程度高，适合流水线生产，因而现今全世界90%以上的汽车车身均使用阴极电泳涂料涂装)。汽车工业的迅猛发展，对阴极电泳涂料性能的要求也越来越高，其中，提高涂料的泳透力是电泳涂装最重要的方向之一
提高阴极电泳涂料的泳透力通常可以从提升电泳漆膜电阻和适当提高槽液电导率两个方面考虑[2]。目前已有研究人员从树脂的角度对提高泳透力进行了一些研究。一般是采用对主链扩链进行控制.降低相对分子质量，提高树脂的电荷密度，并适当
使用强酸，提高乳液电导率的方式提高电泳涂料的泳透率[3]。然而主体环氧树脂相对分子质量的下降会导致电泳涂膜防腐性能的下降，而且过大的电荷密度也可能造成电泳过程中电极反应加剧，使涂膜外观下降。本研究通过将具较大电阻的酚醛树脂改性制备成水分散液4添加到槽液中，在提高泳透力的同时保证了电泳涂料的防腐能力和外观，使得涂膜整体性能得到更好平衡。
1
实验部分
1.1原材料
甲苯二异氰酸酯（TDI)：工业级.韩国韩华石油
作者篇介：邓力（1984一），男，工学顾士，工程师，从事汽车电泳漆开发工作。 54