第40卷第6期 2010年6月
涂料工业
PAINT&COATINGSINDUSTRY
阴极电泳涂料用丙烯酸改性环氧树脂的制备
蒋建平，李小玉（中山火炬职业技术学院，广东中山528436）
Vol.40No.6 Jun.2010
摘要：环氧树脂经扩链改性后，采用丙烯酰胺为交联性功能单体，甲基丙烯酸甲酯、苯乙烯为硬单体、丙烯酸丁酯为软单体，与环氧树脂接枝共聚，制备阴极电泳涂料用丙烯酸改性环氧树脂。漆膜耐水、耐酸、耐碱、耐冲击性好，膜厚19um，附着力1级，硬度3H。单因素实验确定接枝反应的较佳条件为丙烯酰胺的用量为4.0%，引发剂过氧化苯甲酰的加入量为0.15%，接枝温度为115℃。
关键词：环氧树脂：丙烯酸；改性；阴极电泳涂料
文献标识码：A文章编号：0253-4312（2010）06-0044-04
中图分类号：TQ630.4
StudyonthePreparationof AcrylicModifiedEpoxyResin
Usedfor CathodicElectrophoretic Coatings
JiangJianping，LiXiaoyu
(Department of biomedicine,Zhongshan Torch Polytechnic,Zhongshan,Guangdong528436,China)
Abstract:An acrylic modified epoxy resin used for cathodic electrophoretic coating was prepared by use of chain - extended modified epoxy resin as binder backone and grafted with acrylamide as crosslinkable monomer,methyl methacrylate and styrene as hard monomer,and butyl acrylate as soft monomer.The film has the properties of good water, acid and alkali resistance and impact resistance. The Thickness, adhesion and hardness of the film was 19 μm, grade 1 and 3H respectively. The optimum conditions of grafting reac-tion was determined by single factor experiments. The results showed that the amount of benzoperoxide and acrylamide were 0.15%4.0%,respectively at115C.
Key Words:epoxy resin; acrylic acid; modification; cathodic electrophoretic coatings
0引言
阴极电泳涂料采用阴极电泳涂装的方式，具有不腐蚀涂装物、高效、节能及环境友好等优点，已在汽车工业及其他金属涂装领域得到了广泛应用[1]
环氧树脂具有良好的附着力，较强的耐腐蚀性，适宜用于底漆，其缺点是漆膜硬而脆，且耐候性不佳。丙烯酸树脂具有优良的耐腐蚀性、耐紫外光性、耐候性和光泽。两者经配方调节，可得到能制备不同玻璃化温度、不同硬度漆膜的涂料[2-4
为兼顾体系混容性及漆膜的附着性能，实验采用先将低相对分子质量的环氧树脂进行扩链改性，再以内烯酰腰为交联性功能单体，甲基内烯酸甲酯、苯乙烯为硬单体、内烯酸丁酯为软单体，与环氧树脂接枝共聚，制备阴极电泳涂料用丙烯酸改性环氧树脂。
作者简介：等建平（1976一)，女，高级工程师，从事化工教学和科研。 44
1实验部分 1.1主要试剂
环氧树脂E-44：环氧值0.41~0.47，工业级；双酚A、聚乙二醇400、二乙醇胺（DEA）、乳酸：化学纯：苯乙烯（ST）、甲基丙烯酸甲酯（MMA）、丙烯酸丁酯（BA）：分析纯，碱洗；过氧化苯甲酰（BPO）、偶氮二异丁晴（AIBN）：化学纯：丙烯酰胺
（AM）、异丙醇、环已烷、二甲苯：分析纯。 1.2仪器
索氏提取器：浙江杭州旷维实验室设备有限公司：差示扫描量热仪DSC-60：日本岛津公司；FT-IRNicolet5700：美国热电尼高力公司；PHS-25型数显pH计：上海智光仪器仪表有限公司：T1220涂层测厚仪：上海峰志仪器有限公司；漆膜冲击器：上海安锐自动化仪表有限公司：DDS-307电导率仪：上海申骋仪器科技有限公司。