2017年第3期
炼油与化工
REFINING AND CHEMICAL INDUSTRY
MgO改性对Y-AlO：酸性和催化活性的影响
孙雪芹，潘志爽，张爱萍，王智峰(中国石油兰州化工研究中心，甘肃兰州730060）
摘要：采用溶胶一凝胶法制备MgO改性的氧化铝，考察MgO含量对氧化铝酸性、酸类型和催化活性的影响。研究表明，经过M0改性，氧化铝表面的酸类型不变，但在一定程度上改变了-AIO,的酸量和活性，且随着MgO含量的增加，弱酸量基本保持不变，总酸量、强酸量和活性
先降低后升高.在Mg0含量为2.00%左右时达到最小值。关键词：MgO；-Al:0；酸性；催化活性
中图分类号：0643.36
文献标识码：A
文章编号：16714962(2017)03000703
EffectofMgOmodificationonacidityandcatalyticactivityofy-AlO
Sum Xueqin, Pan Zhishuang,Zhang Aiping, Wang Zhifeng
(PetroChina Lanzhou Petrochemical Research Center , Lanzhou 730060, China)
Abstract: MgO modified aluminum was prepared using solgel method. The effects of MgO on its acidity , acid type and eatalytic activity were investigated. Research showed that the surface acid type of aluminum was unchanged after MgO modification, but to some , the acid amount and catalytic activity ofy Al,O, were changed。 With increasing of MgO content, The amount of weak acid was almost unchanged, the total acid content, the amount of strong acid and the catalytic activity first decreased and then increased,
and reached the minimum when MgO content was about 2.00%. Keywords: MgO ;y Al,O, ; acidity; catalytic activity
拟薄水铝石作为催化裂化催化剂关键基质材料，其较强的酸性强度、密度和较多的中大孔孔道结构对改善催化剂综合反应性能具有积极作用降低拟薄水铝石胶溶反应所需无机酸用量可以达到弱化拟薄水铝石酸性的目的，但该措施弱化基质酸性幅度有限，特别是当拟薄水铝石质量波动和催化剂磨损指数偏高时，该技术路线难以满足低基质活性的设计要求，因此在催化裂化催化剂的开发中，采用元系改性拟薄水铝石，调变其表面的酸性，考察改性元素加量对拟薄水铝石酸性活性等变化规律。沈志虹等"研究了-Al:O,中添加MgO来调节表面酸性，发现MgO不改变载体表面酸性，只是减少了强L酸中心。因此，在-AI:0，载体中加人改性元素，主要是调变氧化铝表面酸中心数目和数量，降低载体表面酸量，减少积炭副作用的发生以提高催化剂的选择性和稳定性[2.3]。
1实验部分 1.1实验仪器
万方数据
主要仪器有：烧杯、量筒、布氏漏斗、玻璃棒、研钵、瓷碗、石英碗、吸耳球、移液管、筛子、酸度计、YP15KN型电子天平（上海精密科学仪器有限公司）、HH-2恒温水浴锅（金坛市新航仪器厂）、 JB50-D增力电动搅拌器（上海标本模型厂制造）、 101-2-BS-Ⅱ型电热恒温鼓风于燥箱（上海跃进医疗器械厂）、LH60/15型马弗炉（德国）、ZSXPrimus 型X射线荧光光谱仪（日本Rigaku公司生产）、旋转水热老化装置（北京尔三青绿色化学科技有限公司生产）、布鲁克TENSOR27型红外光谱仪。 1.2样品制备
（1）-Al0,样品的制备。实验取一定量的拟薄水铝石放入马弗炉中，在540℃焙烧2h即可得到-Al:o,样品。
(2）Mg/y-AlO;的制备。称取一定量的拟薄水铝石样品置于反应容器中，按固液比加入蒸馏水，电磁搅拌一定时间后加人改性元素MgCl溶液，继续搅拌，然后接酸铝比加人盐酸酸化成胶，