[摘要]：阐述了感应线图测出由缺陷引起电流扰动导致的磁通变化的理论方法。制作了奥氏体不锈钢材质焊接试块，对焊缝缺陷深度与图形幅值大小之间的关系进行了分析，讨论了影响检测信号的因素和规律。通过试验及检测表明，此方法可以将缺陷检测出来并能确定深度，满足工程检测的要求。
[关键词]：扰动涡流；故障诊断；中冷器；焊缝中图分类号：TK414.2；TH45
5文献标志码：A
文章编号：10062971(2014)04-00058-03
ResearchonFaultDiagnosisoftheCoolerBasedonDis-turbedEddyCurrentAnalysis
SONG Shu-bo', WANG Hai-bo', LIN Hong-wei2
(1.Jilin Institute of Chemical Technology, Jilin 132022, China; 2.Jilin Special Equipment Inspection Center, Jilin 132013, China)
Abstract:In this paper, theoretical method of induction coil to measure magnetic flux changes is introduced, the magnetic flux changes is caused by current disturbance to the defect.An austenitic stainless steel welding test block is made, the relationship be-tween the depth of the weld defect and graphic amplitude size is analyzed, and the effect factors and laws on signal detection is dis-cussed. Through practical testing, it shows that the flaws could be checked out and the depth could be predicted by this method.It meets the requirements of engineering testing.
Key words: disturbed eddy current; fault diagnosis; cooler, weld
1引言
在石油化工生产中广泛的应用压缩机管壳式冷却器，随着使用年限的增加会出现一些故障，比如因振动使换热管与折流板内孔撞击，造成管子磨损、开裂；流动死区处出现换热管腐蚀穿孔或裂开；振动使管子与管板联接处疲劳破坏，管端出现裂开造成渗漏，从而使冷却器失效。目前检修中对管与管板的连接焊缝处可采用交变磁场(ACFM）方法检测，但这种方法对碳钢检测效果可行而对奥民体不锈钢材质不能进行有效检测，针对奥氏体不锈钢材质的换热管与管板连接焊缝处检漏的问题，本文进行了此方面焊缝检测的测试
收稿日期：2014-01-24
压编技术 58Comp
实验，通过试验及应用表明扰动涡流法可有效检测出裂纹等缺陷，检测对象的表面可不做任何处理（如不需耦合剂等），达到工程检测的要求，实
际应用筒易方便。 2原理分析
如图1所示，当有变异（如缺陷）出现时，感应电流的变化引起磁通变化而能被感应线圈检测到。如果激励线圈直径的大小与感应线圈直径大小相差不是很大，图1中所示的磁通的大小及方向各不相同，这样，缺陷导致的磁力线扰动变化因干扰而不易检测出，如何改变感应线圈内大量穿过的方向各异的磁力线的变化影响变得很重要间。研究发现，当激励线圈的直径大小与感应线