第38卷第10期
2010年10月【助剂】
聚氰乙烯 Polyvinyl Chloride
Vol.38，No.10 Oct.，2010
以塑化时问和塑化扭矩为定量指标的润滑平衡规律
刘芳1.2，李杰2，时凯2
（1.北京天加科技有限公司，北京100070；2.北京加成助剂研究所，北京100070）［关键调丁PVC塑料；润清剂；润滑作用；塑化速率；塑化时间；熔体黏度；塑化扭矩
[摘要］讨论了PVC加工过程中物料的塑化情况，以及PVC加工过程的主要影响因素，指出以塑化时间及塑化扭矩为定量指标的润滑平衡规律对PVC润滑配方设计具有参考意义，。
［中图分类号］TQ325.3
0 Lubrication balance law indicated by
plastificationtimeand plastification torque as quantitativeindexes
LIUFangl,LI Jie',SHIKai?
(1.Beijing Tianjia Scicnce and Technology Co.,Ltd.,Beijing 100070,China;
2. Beijing Jiacheng Additive Rcscarch Institute, Beijing 100078, China)
Key words: PVC plastics; lubricant; lubrication; plastification rate; plastification time; melt viscosity; plastification torque
Abstract: The plastification situation of PVC during proccssing was discussed as wcll as the main factors of influencing the processing process of PVC. It was indicated that the lubrication bal-ancc law indicated by plastification time and plastification torque as quantitative indexes had the guiding meaning to the designing of PVC lubrication formula.
挤出机螺杆一般分为输送段、塑化段（亦称压缩段）、计量段（均化段）。PVC物料主要是在塑化段完成塑化；计量段的主要作用是均化PVC树脂，使塑料制品的质量均匀稳定；而螺杆2/3处恰好是塑化段结束、计量段开始的位置，也就是说，该处是 PVC塑化过程基本结束、均化作用即将开始的位置。不言而喻，上述情况是挤出机设计者在理想状态下得到的结论。不同的工艺条件或者内外润滑剂比例使用不当时，PVC混合物的塑化情况与挤出机设计者预期的塑化情况不一定相符。如果加工温度普遍较高或者内润滑剂用量较多、外润滑剂用量较少时，PVC物料在压缩段的1/2长度以前就已经完成了塑化。已经塑化的PVC熔体必然要经过较长
，［收稿日期］2009-07-17
时间的剪切力作用，生成过多的剪切热，导致PVC 过度塑化，甚至发生热分解产生黄线；相反情况， PVC塑化度不够亦会影响制品质量。
由于挤出机中PVC物料的塑化情况无法看到，所以无法对其进行判断。如果有了PVC物料扭矩-时间曲线与挤出机中PVC物料塑化过程近似对应的试验结果，尤其是扭矩一时间曲线上的塑化蜂(即塑化时间及塑化扭矩）处PVC物料与挤出机螺杆2/3处物料塑化情况相似的结论，就可以用扭矩-时间曲线上的塑化时间及塑化扭矩为检测标准，定量地判断某一PVC加工配方中润滑体系或工艺条件的塑化速率及其熔体黏度是否符合特定加工设备及工艺的要求，也就是其塑化时间及塑化扭矩
[作者简介］刘芳（1940一），男，1965年毕业于南开大学化学系，现为北京天加科技有限公司总工程师，长期从事热
稳定剂、润滑剂的研发以及配方改进工作。 24