第38卷第9期 2010年9月
聚氯乙烯 Polyviny! Chloride
Vol.38,No.9 Sep.,2010
新型端胺基聚酰胺一胺树枝状大分子合成研究
黄彩娟·
（贵州大学材料与冶金学院，州贵阳550003)
[关键调］聚酰胺-胺；发散法；已二胺；树枝状大分子
【摘要］研究了以丙烯酸甲酯、已二胺、对苯二酚为原料，采用发散法合成新型端胺基聚酰胺一胺树枝状大分子时，反应条件一一温度、反应时间、催化剂对合成产物的结构的影响。利用该树枝状大分子的活性点分布均匀的特点，通过设计和控制树枝状大分子模板剂来控制纳米粒子材料的形状。
［文章编号】10097937(2010)09003503
[中图分类号】TQ325.3［文献标患码］A
Study on synthesis of a new type of amino-terminated polyamidoamine (PAMAM) dendrimer
HUANGCaijuan
(The Material and Metallurgy College,GuizhouUniversity,Guiyang 550003,China) Key words: polyamidoamine (PAMAM); divergent method;hexanediamine;dendrimer
Abstract: Using methyl acrylate, hexanediamine and hydroquinone as raw materials, a new type of amino-terminated polyamidoamine (PAMAM) dendrimer was synthesized through diver-gent method, Influences of reaction conditions, such as temperature, reaction time and catalyst, on the structure of prepared product were studied. Based on the uniform distribution of active points of dendrimer, the shape of nanoparticle materials was controlled by designing and controlling the dendrimer templates
聚酰胺-胺（PAMAM)树枝状大分子在超分子化学中作为分子自组装的构筑单元，由于其结构的高度对称性、表面极高的官能团密度和分子大小、形状等参数在其合成过程中的可控性，可作为高分子材料PVC的流变学改性剂、PVC材料聚合反应的引发剂和添加剂，同时也是制备PVC材料填充剂纳米二氧化硅的良好偶联剂1-]。树枝状大分子的合成方法主要有发散法[5]、收敛合成法["]、高度核心和支化单体合成法、双倍指数混合生长合成法。笔者主要研究采用发散法合成新型端胺基PAMAM树枝状大分子时，反应条件对树枝状大分子的结构的影响。
1试验方法 1.1试验药品
已二胺（分析纯）、丙烯酸甲酯（分析纯）、对苯二酚（分析纯）、无水甲醇（分析纯）、无水乙醇（分析
［收稿日期］2010-06-20
纯)、甲醇钠(分析纯)。 1.2试验仪器
反应设备：三口烧瓶（250mL）、电热套、智能程序调节仪（LU-960M)、增力电动搅拌器（J-1)、温度指示控制仪（WMZK-01）、集热式磁力加热搅拌器(DF-101S)、智能型数显鼓风于燥箱(JCI-GL)、旋转蒸发器(RE-85Z)。
检测设备：质谱仪（美国ThermoFinnigan LCQ-AdvantageLC/MSAPCI电离源）。
测试条件：甲醇为溶剂，喷雾电压2.0kV，毛细
管温度220℃，毛细管电压28V，管透镜50V。 1.3试验条件
合成0.5代端胺基PAMAM树枝状大分子和 1.0代端胺基PAMAM树枝状大分子的试验条件分别见表1、表2。
[作者简介］黄彩娟(1974一)，女，讲师，主要从事化工材料加工方向的研究工作。
35
万方数据