第38第4期 2010年4月
聚氯乙烯
Polyvinyl Chloride
文石型碳酸钙对PVC热稳定性能的影响
林秀玲1”，胡克良”
Vol.38, No.4 Apr.，2010
（1.安徽理工大学材料科学与工程学院，安徽淮南232001;2.中国科学技术大学，安徽合肥230026）
[关键词]PVC;碳酸钙；文石结构;热稳定性能
[摘要］制备了2种文石型碳酸钙（自制碳酸钙和天然碳酸钙)，并研究了其对PVC热稳定性能的影响，结果表明①碳酸钙结晶受到有机大分子的影响，可形成文石结构的碳酸钙晶体；②文石型碳酸钙不利于PVC热稳定性能的提高。
[中图分类号】TQ325.3
[文献标志码]B
[文章编号］10097937(2010)04002703
Influencesof aragonitetypecalciumcarbonateonthethermal stabilityof PvC
LINXiuling'，HUKeliang
(1. Department of Materials Science and Engineering,
Anhui University of Science and Technology, Huainan 232001, China; 2. University of Science and Technology of China, Hefei 230026, China)
Keywords:PVC;calciumcarbonate;aragonitestructure;thermal stability
Abstract: Two kinds of aragonite type calcium carbonate (i.e. self-made calcium carbonate and natural calcium carbonate) were prepared, and their influences on the thermal stability of PVC were studicd. The results showed that: (1) influenced by organic macro molecules, calcium carbonate crystals with aragonite structure could be formed. (2) aragonite type calcium carbonate was unfa-vorabletothe improvementof thermal stability of PvC
碳酸钙的化学式是CaCO，，其结晶体主要有三方晶类的方解石和斜方晶类的文石。在常温常压下，方解石是稳定型，文石是准稳定型。无论是轻质碳酸钙还是重质碳酸钙，均以方解石为主。生物矿物贝壳属重质碳酸钙，主要含质量分数95%的碳酸钙和少量的贝壳素1)。研究发现，贝壳的无机相为文石相(2-，
笔者制备了2种文石型碳酸钙：①以有机大分子为模板制备的文石型碳酸钙4)（简称自制碳酸钙），②采用淡水珍珠贝壳制备的文石型碳酸钙（简称天然碳酸钙）；探讨了2者对PVC热稳定性能的响，为进一步研制低成本PVC制品莫定了基础。
［收稿日期］2010-01=12
1试验部分
1.1试验原料及仪器
氢氧化钙，分析纯，天津市博迪化工有限公司；蒸馏水，自制；明胶，分析纯，天津市大茂化学试剂厂;PVC固体粉末，中国石化扬子石油化工有限公司；四氢呋喃，分析纯，国药集团化学试剂有限公司；贝壳粉，自制，采自准河岸边。
磁力揽拌器(79-2)，江苏省金坛市荣华仪器制造有限公司；红外光谱仪（NicoletMagna750），美国 Nicolet(尼高力）公司；密封式化验制样粉碎机(F97-I)，南昌光明化验设备有限公司；高温电炉（MHXS-4-10)，江苏煤矿电器厂；X射线衍射仪
[基金项目】安徽省教育厅高校省级自然科学一般研究项目（KJ2008B275），安微省高校青年教师科研”资助计划"项
目（2008jp1038）
[作者简介］林秀玲（1980一)，女，讲师，硕士，主要从事复合材料研究。