第39春第4期
2011年4月【科研与生产】
聚氯乙烯
Polyvinyl Chloride
提高氟乙烯聚合转化率的试验研究
张京友”，许志东
（中国石化股份有限公司齐鲁分公司氯碱厂，山东淄博255400）
［关键词］氯乙烯；聚合；压力：温度；转化率
Vol.39,No.4 Apr.，2011
[摘要］研究了氯乙烯聚合转化率的影响因素，并考察了转化率对PVC颗粒特性的影响情况。在案合温度不变的条件下，氯乙烯的案合转化率随案合反应后期签内压力的降低面增大；提高聚合温度和增加引发剂用量可有效提高聚合反应速率，缩短达到高转化率的时间：转化率宜控制在80%～85%，过高则PVC的增塑剂吸收量降低。
[中图分类号］TQ325.3
［文献标志码】B［文章编号】1009-7937(2011)04-0013-03
Experimental research on improving the plomerization conversion of vinyl chloride
ZhangJingyou，XUZhidong
(Chlor-Alkali Plant,Qilu Branch Co.,SINOPEC,Zibo 255400,China)
Key words: vinyl chloride: polymerization; pressure; temperature; conversion
Abstract: Factors of influencing the plomerization conversion of vinyl chioride were studied, and influences of the convertion on characteristics of PVC particles were investigated. When the polymerization temperature was kept constant, the polymerization conversion of vinyl chloride was increased with the reducing of pressure inside polymerizer in the later polymerization phase. In-e ization rate and shorten the time of achieving high conversion. The conversion was preferably con-trolled at 80% 85%, and over-high conversion could reduce the plasticizcr adsorption of PVC.
氯乙烯悬浮聚合是液态氯乙烯在揽拌作用下分散成液滴、悬浮在水相介质中的聚合过程。整个聚合过程可细分为5个动力学阶段：①第1阶段转化率范围为0～0.1%，该阶段是氟乙烯聚合体系唯一的均相聚合阶段，体系尚未发生沉淀。②第2阶段转化率范围为0.1%～1.0%，在第1阶段末，自由基增长到一定尺度，自身缠结，成为独立的分子聚积体而沉淀出来。③第3阶段转化率范围为1.0%～ 70%，该阶段是氟乙烯聚合最重要的阶段。整个阶段都存在着两个组成恒定的有机相（单体相和PVC 相），反应同时在两相中进行。该阶段结束时的转化率随温度不同而稍有差异。工业生产时，该阶段结束时的转化率为70%左右。④第4阶段转化率范围为70%～85%，第3阶段结束时，液相单体消失，
，［收稿日期］2010-03-03
体系压力开始下降，在该阶段主要由聚合物落胀的单体进行聚合，这种聚合在整个第3阶段都在发生，所不同的是在第4阶段单体的有限供给有效地控制了聚合物内部的反应，此时的单体补充来自气相和悬浮介质中。第5阶段转化率范围为85%～ 10)%，该阶段完全靠气相和悬浮介质单的残余单体从低密度状态扩散进稠密的聚合物固相进行聚合，聚合速度十分缓慢。
根据以上分析，转化率在70%以下时，反应同时在单体相和PVC相中进行。这阶段聚合釜内压力就相当于氯乙烯的饱和蒸气压；转化率达70% 后，单体相消失，只有PVC相，此时的聚合釜内压力相当于PVC相中氯乙烯的分压，而氯乙烯分压与 PVC相中未反应的氯乙烯的量成正比，因此聚合釜
[作者简介］张京友(1964一），男，高级工程师，毕业于青岛化工学院，现任中国石化股份有限公司齐鲁分公司氟磁厂
副厂长，主要从事生产技术管理与科研开发工作。
万方数据
13