第41参第4期 2013年4月
聚氢乙烯
Polyvinyl Chloride
提高氟乙烯转化效率的攻关
邹试，，王定华，岳杏媚
（中盐湖南株洲化工集团有限公司，湖南株洲412004）
【关键词］氯乙烯转化率；氯化汞；触媒
Vol.41. No.4 Apr.,2013
[摘要］针对氰乙烯转化效率低及触媒消耗较高的间题，对转化装置进行了一系列整改，包括提高原料气质量、改善转化器工况、优化转化器操作等。改造后转化器泄漏次数减少，触媒使用寿命延长，触媒单耗降低，节约成本157.81万元/a。
[中图分类号］TQ325.3
[文献标志码]B
[文章编号】10097937(2013)04002204
Breakthrough of increasing vinyl chloride conversion
ZOUBin,WANGDinghua，YUEXingjuan
(Hunan Zhuzhou Chemical Industry Group Co., Ltd., CNSG,Zhuzhou 412004, China) Key words: vinyl chloride; conversion; mercuric chloride; catalyst
Abstract: According to low vinyl chloride conversion and high catalyst cost, reforms on the conversion plant was performed, including improving feed gas quality and converter condition, op timizing converter operation and so on, After the reform, the leakages of converter were reduced, the catalyst life was prolonged, the catalyst cost was decreased, and the production cost was saved by 1.5781million RMB per year.
中盐湖南株洲化工集团有限公司（以下简称中盐株化)现有PVC装置生产能力为20万t/a，其中第1期和第2期装置设计生产能力各10万t/a。配套转化器共60台，其中第1期装置32台（一段16 台，二段16台），第2期装置28台（段16台，二段 12台）。
1转化器运行方面存在的主要问题
(1)要达到20万t/a的生产能力，转化器就必须超负荷运行。主要表现为转化器空间流速高、反应温度偏高、反应后气体中乙炔含量超标，只好靠多消耗触媒来保证生产负荷，致使触媒使用状况恶化，具体表现为触媒汞流失速率加快、触媒使用时间缩短，进而影响生产负荷和装置的长周期稳定运行。
(2)第1期装置于2006年投产，运行时间已达[收稿日期］2012-11~10
6年。随着运行时间的增加，转化器腐蚀加剧，泄漏越来越严重，尤其是2010年，泄漏达54台次。
(3）自2011年下半年乘价格上涨以来，触媒质量明显下降。
①从外观上观察，触媒颗粒不均匀，尤其小颗粒较多，棱角不分明，表观密度增大。
②氟化汞含量一般在10.6%~11.0%（质量分数，下同)，虽在合格范围，但基本在指标下限附近。
③从灰分查定情况来看，灰分质量分数超过 1%，大于指标要求的0.5%。
④从使用效果来看，有些新触媒装进转化器后，反应迟缓，活性不强，表现为反应温度上不去，反应后气体中乙炔含量偏高等。
[作者简介］邹斌(1987一)，男，助理工程师，毕业于山西大学化学化工学院，现于中盐湖南株洲化工集团有限公司从
事PVC生产技术工作。 22
万方数据