第39卷第5期
2011年5月【助剂】
聚氧乙烯
Polyvinyl Chloride
新型引发剂在氟乙烯悬泽聚合中的应用试验
吴仲昆”，许志东
（中国石油化工股份有限公司齐鲁分公司氯厂，山东淄博255400）
【关键词］氯乙烯；引发剂；悬浮聚合;试验
Vol.39, No.5 May，2011
[摘要］通过试验”对过氧化新戊酸叔已酯与偶鼠二异庚睛两种引发剂在氯乙烯悬浮聚合中的应用进行了比较。结果表明：过氧化新戊酸叔已酯的反应活性和相对分子质量比偶氮二异庚睛略低，水溶性略大；在相同条件下，过氧化新戊酸叔已酯的残留率高；在用量（物质的量)相同的条件下，二者使用效果相当。
[中图分类号］】TQ325.3
[文献标志码］B
［文章编号］10097937(2011)05003403
Application test of novel initiators in suspensionpolymerization of vinyl chloride
WUZhongkun，XUZhidong
(Chlor-Alkali Plant，Qilu Branch Co.,SINOPEC,Zibo 255411,China)
Key words: vinyl chloride; initiator; suspension polymerization; test
Abstract: The application effects of two kinds of initiators, i. e. of t-hexyl peroxypivalate(HPV) and azobisisoheptonitrile (ABVN) in suspension polymerization of viny chloride were com-pared by expcriment. Thc results showed that: ① compared with ABVN, HPV had lower reactive activity and relative molecular mass, and bigger water-solubility; ② under the same conditions, HPV had higher residual ratio; ? under the same using amount, the two initiators had the same effect.
中国石油化工股份有限公司齐鲁分公司氟碱厂（简称齐鲁氯碱厂)1*PVC装置聚合引发剂目前采用过氧化二碳酸二-（2-乙基己基）酯（简称EHP）和偶氮二异庚睛（简称ABVN)复合引发体系，但由于ABVN分解后形成具有毒性的氰基，储存时可能产生剧毒氰化氢，在氯乙烯聚合过程中易使产品略微带色，所以笔者根据1"PVC装置的生产实际情况，在广泛调研的基础上，提出了引发体系改进方案：采用EHP和过氧化新戊酸叔已酯（简称HPV）复合引发体系代替原EHP和ABVN复合引发体系，并在中试聚合签上进行了试验，考察HPV在聚合过程中能否满足引发速率高、反应速度快、反应平
稳易控制的要求。 1试验部分 1.1原材料
氯乙烯单体（VCM），≥99.98%（质量分数，下·［收稿日期］2011-0315
同)；去离子水（DW），pH=5～8；聚乙烯醇(KH20)，6%；羟丙基甲基纤维素（E50)，3%；EHP(LB),40%;ABVN(LE),20%;HPV,70%;二Z基
羟胺(DEHA)，20%。 1.2主要设备
采用375L聚合釜，釜径700mm，浆型为两层
两叶平桨，挡板为4块平挡板，垂直釜壁安装。 1.3工艺过程
聚合釜清洗干净后，按配方量向聚合釜内加人去离子水和化学品，封闭人孔。启动真空泵，抽真空至-0.082MPa，并保持2min。向釜内加人配方量的VCM，冷揽15min之后升温至聚合温度，采用 DCS控制聚合反应温度恒定。当聚合釜压降达一定压力时，加入终止剂终止反应，保持10min，回收 VCM，放料，取样，烘干分析。
[作者简介］吴仲昆（1967—），男，2007年毕业于山东理工大学化学工程与工艺专业，现从事生产管理工作。 34