悬浮聚合法氟醋树脂溶解性能的影响因素及解决措施
黄东，
（新辖石河子中发化工有限责任公司，新磁石河子832000）
关键调】氯醋树脂；悬浮案合：溶解性能；解决措施
【摘要】考察了聚合体系、组成均一性、VAc的含量、分子质量分布、杂质粒子对悬浮案合法氯酯树脂溶解性能的影响。结果表明，采取如下措施可提高氯醋树脂的溶解性能：①采用分散剂HPMC（适宜用量为1250μg/g）和偶氮类引发剂，并采用高温、高压的聚合工艺以减少链转移剂的用量；②采用VC连续加料工艺；③氧醋树脂中 VAc的质量分数提高到10%以上；④缩小氰酯树脂分子质量分布宽度；③减少氯醋树脂中的杂质粒子。
【中图分类号】TQ325.3
【文献标志码］B
[文章编号】10097937(2015)04002205
Factors of influencing solubility of suspension polymerizationproduced
vinyl chloride-vinyl acetate resins and solutions
HUANGDong
(Xinjiang Shihezi Zhongfa Chemical Industry Co., Ltd., Shihezi 832000, China)
Key words: vinyl chloride-vinyl acetate resin; suspension polymerization; solubility; solution
Abstract: The effects of polymerization system, compositional homogeneity, VAc content, molec-ular weight distribution and impurity particles on the solubility of vinyl chloride-vinyl acetate ( VC-VAc) resins produced by suspension polymerization method were investigated. The results showed that taking some measures could improve the solubility of VC-VAc resins. The measures included using dispersant HPMC(suitable amount 1 250 μg/g) and azo initiators, carrying out the polymerization at high tempera-ture and high pressure to reduce the amount of chain transfer agents, adopting continuous VC feeding process, increasing the VAc content to more than 10% , narrowing the molecular weight distribution of VC-VAc resins, and reducing the impurity particles in VC-VAc resins.
德国和美国早在1929年就开始生产氟乙烯-醋酸乙烯酯（VC-VAc）共聚树脂（以下简称氯醋树脂），是较早工业化的PVC共聚树脂，也是PVC共聚树脂中产量较大的共聚树脂。由于在PVC分子链中嵌人了醋酸乙烯酯片段，减弱了原来分子的极性，降低了分子间的引力，因此氟醋树脂具有内增塑作用，可提高PVC树脂的增塑剂吸收速度和在溶剂中的溶解速度，增加与各种基材的粘接力，在油墨及涂料产品中应用较为广泛。
[收籍日期]2015=02-13
在作为原料制备油墨、涂料、粘接剂时，必须将氟醋树脂溶解于酮类、酯类等有机溶剂中，因此要求氟醋树脂的溶解性能好，溶液应透明。氯醋树脂的溶解性能主要通过其溶液的透明度、粒子细度来反映。氟醋树脂的溶解性能除了与组成和分子质量有关外，还与颗粒特性（例如形态、多孔性、孔隙均匀性等)有着密切的关系。如何确保悬浮法氯醋树脂具有良好的溶解性能是生产过程中需要解决的一大难题。笔者着重对悬浮聚合法氯醋树脂溶解性能的影响因素进