第44卷第11期
2016年11月【助剂】
聚氯乙烯 Polyvinyl Chloride
低汞触媒规模化应用过程中的问题探讨
王洪欣”，杨超松，汪福兵
（新疆中泰（集团）有限任公司，新疆乌鲁木齐830009）
【关键词］低汞触媒；规模化；转化率；电石法PVC
Vol.44,No.11 Nov.,2016
【摘要】针对低汞触媒在规模化应用过程中出现的间题进行探讨，提出解决措施。当生产装置出现波动时，通过保证转化热水温度、控制单台转化器通量、优化转化器运行模式等方法，提高低汞触媒的催化效率。
【中图分类号】TQ325.3【文献标志码】B【文章编号】10097937(2016)11003303
Discussion of problems occured inlarge-scale application of low-levelmercury catalysts
WANG Hongxin，YANG Chaosong,WANGFubing
（XinjiangZhongtai（Group）Co.，Ltd.，Urumqi 830009，China）
Key words: low-level mercury catalyst; large-scale; conversion rate; carbide-method PVC
Abstract: The problems occured in large-scale application of low-level mercury catalysts were diss-cussed, and the solving measures were proposed. When production fluctuated, the catalytic efficiency of low-level mercury catalysts were improved by stabilizing temperature of hot water used for conversion, controlling flux of single convertor, optimizing operation mode of convertors and so on.
我国PVC生产工艺主要有乙烯法和电石法，但由于我国“多煤、贫油、少气”的资源和能源结构，电石法PVC成为我国PVC工业的主流工艺(1)。2015 年，我国PVC生产能力为2348万Va其中电石法 PVC生产能力为1918万Va，乙烯法生产能力为 430万Va，电石法PVC占总生产能力的82%[2]。电石法PVC是我国耗汞量最大的行业，汞资源消耗量占我国汞资源消耗量的60%，占世界汞消耗量的 30%[3]】，对汞资源的过度消耗和汞污染成为电石法 PVC发展的巨大障碍。为了控制和减少汞排放，国家工信部、环保部于2010年明确要求电石法PVC 企业要逐步实现触媒低汞化，2012年低汞触媒使用率达到50%，2015年达到100%，在2020年左右实现低汞触媒固秉化，最后实现无秉化[3)。2013年 140多个国家签署的旨在全球范围内控制和减少汞排放的国际公约《水保条约》[3]，给电石法PVC工艺带来了巨大的压力。
新疆中泰（集团）有限责任公司下属子公司新疆华泰重化工有限责任公司（以下简称华泰公司）
【收稿日期】2016-08-25
PVC树脂生产规模为75万Va，为了积极响应国家及行业号召，2010年开始试用低汞触媒（符合HG/ T4192—2011《氧乙烯合成用低汞触媒》要求）， 2013年通过实施高汞触媒零采购方案，加快了触媒低汞化的实施进度，2014年底全部使用了质量分数
为4.0%~6.5%的低汞触媒。 1原材料控制
1.1严格控制触媒水含量
1g氯化汞可溶于13.5mL水，过高的水含量会使氯化汞的有效浓度降低，影响触媒的使用效率。而在生产中，触媒在使用前均会先用氯化氢活化，氯化氢与水结合生成盐酸，在同离子效应下会加剧氯化汞的溶解；同时，生成的盐酸也会对转化器列管造成腐蚀，影响转化器正常使用。因此，华泰公司严格要求人厂的触媒含水质量分数在0.3%以下；同时，
在触媒活化前，用热氮气进行吹扫，降低水含量。 1.2触媒烧失率及机械强度
氯化氢与乙炔反应生成氯乙烯是一个放热过