氣化聚乙烯傅里叶变换红外光谱分析方法的改进
韩风”，杨雷，张坤明，董军宁，屈文召
（潍坊亚星化学股份有限公司，山东潍坊261031）
关键词氯化聚乙烯;红外光谱制样方法结构分析
摘要用傅里叶变换红外光谱仪分析氯化聚乙烯的结构，考察制样方法及样品膜厚度对测试结果的影响结果表明：用热压膜制样方法所得试样的红外谱图清晰、准确，信息全面；样品膜厚对测试结果会产生影响，厚度为 0.015~0.05mm时，所得红外谱图清晰，一致性好。
［中图分类号]TQ325.12；TQ014［文献标志码］B
［文章编号］1009—7937(2013)08—0036—05
Improvements on methods of analyzing the structure of chloroinatedpolyethylene
by Fourier transform infrared spectrometer
HANFeng,YANGLei,YANGKunming,DONGJunning,QUWenzhao
(WeifangYaxingChemical Co.Ltd.，Weifang261031，China）
Key words : chlorinated polyethylene ; infrared spectrum ; sample preparation method ; structur
alanalysis
Abstract : The structure of chloroinated polyethylene was analyzed by using Fourier transform infrared spectrometer , and effects of sample preparation methods and sample thickness on determi-nation results were investigated . The results showed that the infrared spectra of samples obtained by hot press were clear , accurate and informative ; the thickness of sample could influence the determi, nation results , and infrared spectra with high definition and good consistency could be obtained when the thickness was between 0 .015 and 0 .05 mm .
红外光谱属于分子光谱，它作为“分子的指纹” 广泛用于分子结构和物质化学组成的研究。测试原理为：当红外光谱照射到试样上时，试样中分子振动吸收特定波长的红外光而形成了有序的红外谱带，根据谱带频率、强度和形状可以判定试样的结构和组成。
在红外光谱的测试中，制样技术对测试结果会产生很大影响，同一个样品，采用不同的制样技术，可能会得到不同的光谱图，这在红外光谱的测试中经常遇到。因此，在具体的测试过程中，要根据样品的特性和要求，采用合适的制样方法
氯化聚乙烯是一种性能优异的高分子材料，广泛用于橡胶、塑料和其他特种制品中，它又是一种弹
*［收稿日期］2013—07—04
性体材料。为了能准确获得氯化聚乙烯产品信息笔者采用不同的方法制样，测试其红外光谱，比较不同方法的差异，从而确定氯化聚乙烯结构的最优测试方法。
1试验部分 1.1原料
氯化聚乙烯，潍坊亚星化学股份有限公司;其他
样品，市售。 1.2仪器
傅里叶变换红外光谱仪，ThermoNicoletIS10，测试范围400～4000cm-，分辨率4，扫描次数
[作者简介］韩风（1965一），女，高级工程师，1989年毕业于山东工业大学化工系，现主要从事氯化聚乙烯产品开发和
应用研究工作。 36