第42卷第11期 2014年11月
聚氯乙烯 Polyviny! Chloride
氟乙烯生产装置中换热器泄漏原因及改造
孔范录*，海阳，何永会
（新疆中泰（集团）有限责任公司，新疆岛鲁木齐830000）
Vol.42,No.11 Nov.,2014
[关键调】PVC；氟乙烯；换热器；泄漏；改造
[摘要】对电石法氯乙烯生产过程中换热器泄漏的原因进行了试验分析，发现泄漏的列管在物料人口处堵塞严重，而中部和物料出口附近相对干净，分析了列管中堵塞物的组成及成因，并提出了预防泄漏的措施。
【中图分类号】TQ222.42;TQ051.6【文献标志码】B【文章编号】10097937(2014)110034-04 Reasons for the leakage of heat exchangers in vinyl chloride production
and improvements on them KONGFanlu,HAIYang,HEYonghui
(Xinjiang Zhongtai （Group) Co., Ltd., Urumqi 830000, China)
Key words: PVC; vinyl chloride; heat exchanger; leakage; transformation
Abstract: Reasons for the leakage of heat exchangers in vinyl chloride production were analyzed through experiments. The leaked tubes were seriously blocked near feedstock inlet port, while they were clean in the middle and near material outlet port. The composition of blockages and their forming causes were analyzed. Improvement measures were proposed.
列管式换热器是化工行业应用较为广泛的换热器之一。因构造、材质、使用条件和冷却水质等因素，换热器管束、管口、管板处经常会发生泄漏，使物料进人冷却水系统，既污染环境又造成物料浪费，还会严重影响企业稳定生产，甚至会导致恶性的安全生产事故。目前，电石法PVC行业由于生产规模大，一般各厂家都没有备用设备。为有效降低由于换热器故障带来的生产装置停车，下面以一起换热器泄漏事故作为典型案例进行分析，供大家参考。
1
换热器在精馏系统中的配置及管理现状列管式换热器在氯乙烯精馏工序应用较多，按
20万aPVC生产能力计，约有30台碳钢换热器。采用乙炔合成的氯乙烯成分较为复杂且在设备内流速过低，循环水质有问题，均容易造成污堵结垢，形成垢下腐蚀。所以把精馏工序换热器管理好并不是一件容易的事情。通过与同行业企业进行交流发现，目前换热器的管理现状及技术手段有：加强工艺管理，增加备用设备，对换热器列管进行防腐涂层处理，定期分析冷却水中的氟乙烯含量，将列管式换热
，【收稿日期］2014-04-10
器改为空气冷却器，循环水定期调压冲洗等。总体来说，这些方法能有效避免生产装置频繁停车检修
的问题，但比较被动，而且会增加-一定的投资。 2
试验分析
目前，新疆中泰（集团）有限责任公司对换热器泄漏的监测一般是按周期分析冷却水中氧氟乙烯的含量。某日检测到7C冷却水中氯乙烯质量分数高达 40.62%，对7℃冷却水罐进行充氮置换并停用此台全凝器，检查发现全凝器有6根列管泄漏。拆下全凝器封头后发现列管堵塞比较严重，尤其是物料进口处；封头杂物较多，锈迹斑斑；而列管中部及物料出口附近相对干净。
分别在全凝器物料进口端的上部列管、中部列管、下部列管和封头的污垢中取样，分析过程与结果如下。
异物外观及物理化学性质
2.1
送检的异物标本为黄褐色夹杂灰白色的片状固体，难溶于水，能与盐酸、硫酸发生反应，并产生气体。尤其是异物和盐酸反应时放出臭鸡蛋味气体，